First-principles study of Ca{sup 2+} and Mn{sup 2+} substituents in KTaO{sub 3}
The structural properties, energetics, and dynamics of Ca{sup 2+} and Mn{sup 2+} substituents in KTaO{sub 3} are investigated from first principles. It is found that Ca substitutes for both K and Ta ions. Oxygen vacancies bind to isolated Ca ions residing at Ta sites, causing off-center Ca displacement and forming large dipoles. There is also evidence that oppositely charged defects may cluster together. Our calculations predict that the activation energy for dipole reorientation via oxygen vacancy hopping within the first-neighbor shell of Ta-substituting Ca or Mn exceeds 2 eV. On the other hand, Mn{sup 2+} substituting at the K site displaces off center along the (100) direction, also forming a dipole. This dipole can reorient via Mn hopping motion with an activation energy of {approx}0.18 eV, in reasonable agreement with experiments. We argue that, in general, metal ion hopping at the A site, not oxygen vacancy hopping, is responsible for the small activation energies found in experiments.
- Sponsoring Organization:
- (US)
- OSTI ID:
- 40205459
- Journal Information:
- Physical Review B, Vol. 63, Issue 13; Other Information: DOI: 10.1103/PhysRevB.63.134415; Othernumber: PRBMDO000063000013134415000001; 081110PRB; PBD: 1 Apr 2001; ISSN 0163-1829
- Publisher:
- The American Physical Society
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ferroelectric-to-Relaxor Crossover and Oxygen Vacancy Hopping in Compositionally-Disordered Perovskites - KtA(1-x)Nb(x)O(3):Ca
Ferroelectric-to-relaxor crossover and oxygen vacancy hopping in the compositionally disordered perovskites KTa{sub 1-x}Nb{sub x}O{sub 3}:Ca