HIGH PURITY URANIUM COMPOUNDS. Final Report
Uranium-aluminum compounds were prepared by solidsolid reaction of aluminum powder and uranium hydride; x-ray-diffraction patterns showed that single phases of UAl/sub 2/, UAl/sub 3/, and UAl/sub 4/ could be achieved. The uranium-beryllium compound, UBe/sub 1//sub 3/, was prepared by solid-solid reaction of berylllum powder and uranium hydride. The uranium-boron compounds, UB/sub 2/ UB/sub 4/, and UB/sub 1//sub 2/ were prepared by solid reaction, and single borides were obtained; carbon contamination was especially serious in these samples. The uranium-carbon compounds, UC and UC/sub 2/, were prepared by solid-solid reactlons to 1200 deg C; the x-ray-diffraction patterns showed a mixture of phases, and higher temperatures are probably required. The uranium- nitrogen compounds, UN and UN/sub 2/, were prepared by reaction of uranium with ammonia at 850 deg C for UN/sub 2/ and subsequent heating of that product in vacuum for UN. The uranium-selenium compounds, USe and USe/sub 2/, were prepared in very small samples; the violence of the reaction of selenium with uranium hydride and the lack of availability of hydrogen selenide limits the size of preparations. The uranium-silicon samples, USi/sub 2/ and USi/sub 3/ were prepared by solid-solid reaction of UH/sub 3/ and 8i; numerous attempts were made to prepare U8i. One of the USi/sub 2/ samples was alpha -USi/sub 2/ and the other was beta -USi/sub 2/. The uranium-sulfur compounds, US and US/sub 2/, were prepared; US/sub 2/ was prepared by forming unanium hydride in a flow furnace and then reacting the hydride with hydrogen sulfide; US was prepared by reacting some of the US/sub 2/ with UH/sub 3/. (auth)
- Research Organization:
- SRI International, Menlo Park, CA (United States)
- DOE Contract Number:
- W-31-109-ENG-38, SUBCONTRACT 31-109-38-1030
- NSA Number:
- NSA-15-018022
- OSTI ID:
- 4018241
- Report Number(s):
- ANL-6339
- Resource Relation:
- Other Information: For Argonne National Lab. Orig. Receipt Date: 31-DEC-61
- Country of Publication:
- United States
- Language:
- English
Similar Records
FURTHER STUDIES OF SINTERED REFRACTORY URANIUM COMPOUNDS
DISPERSIONS OF URANIUM CARBIDES IN ALUMINUM PLATE-TYPE RESEARCH REACTOR FUEL ELEMENTS
Related Subjects
ALUMINUM COMPOUNDS
AMMONIA
BERYLLIUM COMPOUNDS
BORIDES
BORON COMPOUNDS
CARBON
CHEMICAL REACTIONS
CONTAMINATION
DIFFRACTION
FURNACES
HEATING
HYDROGEN SULFIDES
NITROGEN COMPOUNDS
POWDERS
PREPARATION
SELENIDES
SELENIUM COMPOUNDS
SILICON COMPOUNDS
SOLIDS
SULFUR COMPOUNDS
URANIUM CARBIDES
URANIUM COMPOUNDS
URANIUM HYDRIDES
VACUUM
X RADIATION