Micromechanical behavior of polymer interface reinforced with copolymers
Conference
·
OSTI ID:400632
- State Univ. of New York, Stony Brook, NY (United States)
The fracture toughness of interface reinforced with dps-b-dpmma copolymer between immiscible polymers of PS and PMMA is tested by asymmetric double cantilever beam. The local deformation field at the interfacial crack tip is determined by the technique of SIEM. Normal and tangential crack opening displacements are calculated. A weak singularity is shown to exist near crack tip. Direct observation on the fracture process inside an environmental scanning electron microscope shows the large effect of mode mixity.
- OSTI ID:
- 400632
- Report Number(s):
- CONF-951155--; ISBN 1-55899-312-6
- Country of Publication:
- United States
- Language:
- English
Similar Records
Asymmetric Double Cantilever Beam Test to Measure the Toughness of an Alumina/Epoxy Interface
On the stress singularity at the interfacial crack tip -- An experimental study
Deformation micromechanisms in polymeric matrices and carbon of fibre-reinforced composites
Technical Report
·
Sat Nov 30 23:00:00 EST 2019
·
OSTI ID:1595916
On the stress singularity at the interfacial crack tip -- An experimental study
Conference
·
Fri Dec 30 23:00:00 EST 1994
·
OSTI ID:89886
Deformation micromechanisms in polymeric matrices and carbon of fibre-reinforced composites
Thesis/Dissertation
·
Sat Dec 31 23:00:00 EST 1988
·
OSTI ID:7122019