SUMMARY TECHNICAL REPORT FOR THE PERIOD JANUARY 1, 1961-MARCH 31, 1961
Uranium and TBP Recovery from Waste Solvent. Laboratory and pilot-scale tests were carried out which demonstrated (1) that uranium in waste solvent can be removed by slurrying the solvent with activated charcoal, filtering the slurry, and washing the slurry with water and 3% Na/sub 2/CO/sub 3/ and (2) that TBP can be recovered from the waste solvent by splitting the solvent with HCl and distilling the TBP-rich phase. Improvement of Green Salt Quality. Denitration of ammonium uranyl trinitrate yielded a light, finely divided form of gamma -UO/ sub 3/ with a surface area higher than that of conventional batch pot powder; however, its reactivity in reduction and hydrofluorination tests was only moderately higher in comparison. Oxidation-reduction cycles were found to increase the reactivity of UO/sub 2/ toward hydrofluorination. The properties of various UO/sub 2/ samples were determined and correlated with the preparative methods used. Dehydration of Winlo Green Salt. About 27 tons of Winlo green salt was successfully dehydrated to a water content of -0.04% in a hydrofluorination reactor bank in the Green Salt Plant. Recovery of Uranium from MgF/sub 2/ Slag. A process for continuously digesting MgF/sub 2/ slag for uranium recovery was successfully tested on a plant scale. In this process, a water slurry of slag is transferred at a fixed rate and reacted with HCl, and the controlled feed rate reduces the hydrogen concentration. Graphite Liner for Bomb Reduction of Green Salt. An evaluation was made on machined graphite as a replacement for jolt-packed MgF/sub 2/ presently used to line reduction vessels for uranium metal production. Best results were obtained with a onepiece graphite liner fitted inside a steel vessel with an annulus of MgF/sub 2/ between liner and pot. Effects of Feed Material on Ingot Chemical Purity and Yields. The effects of various types of uranium feed stock on the chemical purity and yield of ingots were studied. The following results were obtained: (1) The H content was higher in ingots cast from melts contairing more derby material, (2) the O, N, and C contents of samples from ingot tops were signiicantly lower than those from ingot bottoms, (3) the crude ingot yields were lowest for pigots, briquettes, and heat-shocked grade III derbies, (4) pigots were deleterious to ingot chemical purity, (5) degreased drip crops and dingot extrnsion scrap were deleterious to core-to-good-core yield. Alpha Annealing of Uranium. The effect of a high alpha temperature anneal on the structure and growin index of beta heat treated uranium was evaluated. It was found that longer alpha annealing times gave greater recrystallization and that higher temperatures gave more rapid recrystallization. Delays of up to 6 months between beta heat treatment and alpha anneal did not affect either the recrystallization or the growth index. Billet Drilling. A LeBlond-Carlstedt Rapid Borer was tested as a urarium billet drilling machine and found to give satisfactory results, although some tool breakage occurred. (D.L.C.)
- Research Organization:
- National Lead Co. of Ohio, Cincinnati
- DOE Contract Number:
- AT(30-1)-1156
- NSA Number:
- NSA-15-019457
- OSTI ID:
- 4005092
- Report Number(s):
- NLCO-826
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-61
- Country of Publication:
- United States
- Language:
- English
Similar Records
SUMMARY TECHNICAL REPORT FOR THE PERIOD OCTOBER 1, 1959 TO DECEMBER 31, 1959
SUMMARY TECHNICAL REPORT FOR THE PERIOD JANUARY 1, 1959 TO MARCH 31, 1959