Crystal and magnetic structures of the colossal magnetoresistance manganates Sr{sub 2{minus}{ital x}}Nd{sub 1+{ital x}}Mn{sub 2}O{sub 7} ({ital x}=0.0, 0.1)
- Inorganic Chemistry Laboratory, University of Oxford, South Parks Road, Oxford OX1 3QR (United Kingdom)
- Institut Laue-Langevin, P.O. Box 156, 38042 Grenoble Cedex 9 (France)
Neutron powder diffraction techniques have been used to refine the crystal and magnetic structures of the Ruddlesden Popper (RP) compounds Sr{sub 2{minus}{ital x}}Nd{sub 1+{ital x}}Mn{sub 2}O{sub 7} ({ital x}=0.0, 0.1), which show colossal magnetoresistance below 100 K. Samples of both compositions have been shown to be biphasic, although in each case both phases are of the RP type and have very similar structural parameters. Only one phase in each sample shows long range magnetic order. For {ital x}=0.0, the Mn cations and the Nd cations in the rocksalt layers of the structure are antiferromagnetically ordered in a noncollinear magnetic structure below 28 K; the Nd cations within the perovskite blocks do not show long range magnetic order. In the temperature range 28{le}T/K{le}137, only the Mn cations are ordered. The decoupling of the Nd cations is accompanied by a rotation of the Mn moments from a direction close ({phi}=27{degree}) to the {ital z} axis into the {ital xy} plane. A similar temperature dependence is seen in the case {ital x}=0.1, although the ordered components of the cation moments are much reduced and the low temperature phase has a collinear magnetic structure with the moments aligned along {ital z}. The magnetotransport properties of these samples are discussed in the light of their crystal and magnetic structures. {copyright} {ital 1996 The American Physical Society.}
- OSTI ID:
- 399817
- Journal Information:
- Physical Review, B: Condensed Matter, Vol. 54, Issue 22; Other Information: PBD: Dec 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Band metamagnetism and related phenomena in Er(Co{ital {sub 1{minus}x}}Si{ital {sub x}}){sub 2}
Preparation and transport properties of single-phase TlBa[sub 1+[ital x]]La[sub 1[minus][ital x]]CuO[sub 5] (0[le][ital x][le]0. 5)