Enhanced magnetoresistance in YBa{sub 2}Cu{sub 3}O{sub 7}/Nd{sub 0.7}Sr{sub 0.3}MnO{sub 3} heterostructures using magnetic flux focusing
- Department of Physics, Center for Superconductivity Research, University of Maryland, College Park, Maryland 20742 (United States)
Enhanced low field magnetoresistance (MR) in Nd{sub 0.7}Sr{sub 0.3}MnO{sub 3} (NSMO) has been achieved by using high-{ital T}{sub {ital c}} superconducting flux focusing devices made of YBa{sub 2}Cu{sub 3}O{sub 7}(YBCO)/NSMO heterostructures. Two kinds of flux focusing schemes, gap, and washer devices, have been used where an applied magnetic field is expelled from patterned YBCO pads and focused onto a bridge of NSMO film. Using such a magnetic lens, at temperatures below 77 K {approximately}800{percent} enhancement in MR={minus}({ital R}{sub {ital H}}{minus}{ital R}{sub 0})/{ital R}{sub 0} was observed for different samples. This corresponds to more than 10{percent} change in the MR of NSMO in the presence of 200 G. For the maximum MR response in NSMO, the YBCO/NSMO heterostructures were deposited on (100) LaAlO{sub 3} substrate by pulsed laser deposition {ital in} {ital situ} so that the peak resistance temperature ({ital T}{sub {ital p}}) of NSMO was below the superconducting transition temperature ({ital T}{sub {ital c}}) of YBCO. {copyright} {ital 1996 American Institute of Physics.}
- OSTI ID:
- 397398
- Journal Information:
- Applied Physics Letters, Vol. 69, Issue 22; Other Information: PBD: Nov 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Transport properties of La{sub 0.7}Sr{sub 0.3}MnO{sub 3}/YBa{sub 2}Cu{sub 3}O{sub 7-δ} (LSMO/YBCO) heterostructure
Effect of superconducting spacer layer thickness on magneto-transport and magnetic properties of La{sub 0.7}Sr{sub 0.3}MnO{sub 3}/YBa{sub 2}Cu{sub 3}O{sub 7}/La{sub 0.7}Sr{sub 0.3}MnO{sub 3} heterostructures