A comparison of low-chromium and high-chromium reduced-activation steels for fusion applications
Ferritic steels have been considered candidate structural materials for first wall and blanket structures for fusion power plants since the late 1970s. The first steels considered in the United States were the conventional Cr-Mo steels Sandvik HT9 (nominally 12Cr-1Mo-0.25V-0.5W-0.5Ni-0.2C, here designated l2Cr-1MoVW), modified 9Cr-1Mo steel (9Cr-1Mo-0.2V-0.06Nb-0. IC, designated 9Cr-1MoVNb) and, to a lesser extent, 2 1/4Cr-1Mo steel (2.25Cr-Mo-0.1C). All compositions are in wt. %. The normalized-and-tempered 9 and 12Cr steels had a tempered martensite microstructure, and the normalized-and-tempered 2 1/4 Cr steel had a tempered bainite microstructure. This report describes chromium steels tested in normalized and tempered conditions. Miniature tensile and Charpy specimens were tested.
- Research Organization:
- Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 390644
- Report Number(s):
- CONF-961020--1; ON: DE97000325
- Country of Publication:
- United States
- Language:
- English
Similar Records
Neutron irradiation effects on the ductile-brittle transition of ferritic/martensitic steels
Development of low-chromium, chromium-tungsten steels for fusion