Fractography, fluidity, and tensile properties of aluminum/hematite particulate composites
- R.V. Coll. of Engineering, Bangalore (India). Dept. of Mechanical Engineering
This paper examines the effect of hematite (iron oxide) particles on the fluidity of the molten composite as well as the tensile properties and fracture behavior of the solidified as-cast aluminum composites. The percentage of hematite in the composite was varied from 1 to 7% in steps of 2% by weight. The vortex method was employed to prepare the composites. It followed from the results obtained that the ultimate tensile strength and Young`s modulus of the composite increased while the liquid fluidity and solid ductility decreased with the increase in hematite content in the composite specimens. The fluidity of the liquid was greater in a metal mold than in a sand mold, and it decreased with an increase in reinforcing particle size and increased with pouring temperature. The presence of the reinforcing particles altered the fracture behavior of the solid composites considerably. Final fracture of the composite occurred due to the propagation of cracks through the matrix between the reinforcing particles.
- OSTI ID:
- 364018
- Journal Information:
- Journal of Materials Engineering and Performance, Vol. 8, Issue 3; Other Information: PBD: Jun 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fabrication and mechanical behaviour of aluminum matrix composite materials
Fabrication and mechanical behavior of aluminum-matrix composite materials