Fatigue acceptance test limit criterion for larger diameter rolled thread fasteners
This document describes a fatigue lifetime acceptance test criterion by which studs having rolled threads, larger than 1.0 inches in diameter, can be assured to meet minimum quality attributes associated with a controlled rolling process. This criterion is derived from a stress dependent, room temperature air fatigue database for test studs having a 0.625 inch diameter threads of Alloys X-750 HTH and direct aged 625. Anticipated fatigue lives of larger threads are based on thread root elastic stress concentration factors which increase with increasing thread diameters. Over the thread size range of interest, a 30% increase in notch stress is equivalent to a factor of five (5X) reduction in fatigue life. The resulting diameter dependent fatigue acceptance criterion is normalized to the aerospace rolled thread acceptance standards for a 1.0 inch diameter, 0.125 inch pitch, Unified National thread with a controlled Root radius (UNR). Testing was conducted at a stress of 50% of the minimum specified material ultimate strength, 80 Ksi, and at a stress ratio (R) of 0.10. Limited test data for fastener diameters of 1.00 to 2.25 inches are compared to the acceptance criterion. Sensitivity of fatigue life of threads to test nut geometry variables was also shown to be dependent on notch stress conditions. Bearing surface concavity of the compression nuts and thread flank contact mismatch conditions can significantly affect the fastener fatigue life. Without improved controls these conditions could potentially provide misleading acceptance data. Alternate test nut geometry features are described and implemented in the rolled thread stud specification, MIL-DTL-24789(SH), to mitigate the potential effects on fatigue acceptance data.
- Research Organization:
- Knolls Atomic Power Lab. (KAPL), Niskayuna, NY (United States)
- Sponsoring Organization:
- USDOE Assistant Secretary for Nuclear Energy, Washington, DC (United States)
- DOE Contract Number:
- AC12-76SN00052
- OSTI ID:
- 350965
- Report Number(s):
- KAPL-P-000168; CONF-970535-; K-97052; ON: DE99001901; TRN: AHC29921%%151
- Resource Relation:
- Conference: 7. ASTM symposium on composites: fatigue and fracture, St. Louis, MO (United States), 6-8 May 1997; Other Information: PBD: May 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Benefits of thread rolling process to the stress corrosion cracking and fatigue resistance of high strength fasteners
Stress intensity factor solutions for cracks in threaded fasteners