Characteristics of Al:Mg alloy wire-array z-pinches on the Z generator
- Sandia National Labs., Albuquerque, NM (United States); and others
The characteristics of 95% Al:5% Mg alloy wire-array z-pinches formed by the Z generator and their associated x-emission are discussed. The arrays consisted of 180 to 266 wires, with each wire being 20-mm long and mounted at radii of 15, 20, or 25 mm. The implosion time of the loads explored was maintained at {approximately}106 ns by keeping M*R*R constant. M is the array mass that decreased from 7.1 to 4.2 to 2.6 mg as the radius R was increased. Current at the load was measured by B-dot monitors, and piezo-electric pressure gauges. These monitors showed that peak currents of {approximately}19 MA were generated in agreement with Screamer power-flow simulations. The temporally-resolved radiation field was measured by spatially-integrating resistive bolometers, filtered XRDs, and PCDs in 12 discrete channels that spanned the energy range 5 eV to 7 keV. Preliminary analysis indicates that the total radiated energy generated is of the order of 1 MJ and produces a total x-ray power on the order of 65 TW. The K-shell energy yield shows a strong dependence on mass increasing from {approximately}90 to {approximately}200 kJ as the mass decreases from 7.1 to 2.6 mg. Opacity effects are manifested by the share of Mg radiation greatly exceeding its 5% number ratio. Over this range, the associated FWHM of the K-shell emission decreases from 20 to 13 ns and the peak K-shell power increases from 4 to 12 TW, respectively, The x-ray images suggest the presence of a Rayleigh-Taylor instability. Two-dimensional radiation-magnetohydrodynamic simulations in the R-Z plane give insight into the mass distribution arising from this instability.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 346910
- Report Number(s):
- CONF-980601-; TRN: 99:006154
- Resource Relation:
- Conference: 25. international conference on plasma science, Raleigh, NC (United States), 1-4 Jun 1998; Other Information: PBD: 1998; Related Information: Is Part Of IEEE conference record -- Abstracts. 1998 IEEE international conference on plasma science; PB: 343 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Symmetric aluminum-wire arrays generate high-quality Z pinches at large array radii
Characteristics and scaling of tungsten-wire-array z-pinch implosion dynamics at 20 MA