Compositional instability of {beta}-phase in Ni-Mn-Ga alloys
- Inst. of Magnetism, Kiev (Ukraine)
The ferromagnetic Heusler alloys of stoichiometric Ni{sub 2}MnGa and nonstoichiometric Ni-Mn-Ga chemical compositions though not containing a noble-metal, indeed, belong to {beta}-alloys which lattice stability is decided by the Hume-Rothery mechanism: electron concentration e/a measuring the decrease of the electron energy due to the pseudogap formation and size factor. The intriguing feature of Ni-Mn-Ga alloys similarly to Ti-Ni, Cu-Al-Be and Ni-Al alloys arises that transformation temperature, M{sub s}, is dramatically dependent on concentration reflecting an extremely high sensitivity of the lattice stability toward the content variation. The main purpose of present paper is an analysis of previous data concerning the compositional dependence of M{sub s} from the viewpoint of searching for empirical correlation between the electron concentration and stability of {beta}-phase in Ni-Mn-Ga system. This analysis will provide a confirmation of the feasibility of a reasonable explanation of seemingly random collection of alloys grouped with respect to their M{sub s} values as well as other features. The alloys of compositional range studied previously are added here to a few alloys including ones doped with V and Ge to ensure the decisive role of e/a ratio on M{sub s}. Original results about the temperature dependent resistance behavior are presented as well.
- OSTI ID:
- 338404
- Journal Information:
- Scripta Materialia, Vol. 42, Issue 5; Other Information: PBD: 5 Feb 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural and Electronic Investigations of Complex Intermetallic Compounds
The concept of the approximants of quasicrystals