Procurement of V-Cr-Ti alloys to study minor variations on V-4Cr-4Ti
- Oak Ridge National Lab., TN (United States)
The alloys V-6Cr-3Ti, V-4Cr-4Ti-Si, V-6Cr-6Ti, and V-3Cr-3Ti, were prepared by Teledyne Wah Chang Albany Corp. in 1994. Plate and sheet ranging from 0.76 mm to 6.25 mm with residual material being left in 12--20 mm thick bar were fabricated. Although the heats were prepared on a pilot plant scale using different equipment, an effort was made to keep the processing as close to Wah Chang Heat 832665, the reference fusion heat of V-4Cr-4Ti, as possible.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- OSTI ID:
- 335381
- Report Number(s):
- DOE/ER-0313/23; ON: DE98004697; TRN: 99:005171
- Resource Relation:
- Other Information: PBD: Mar 1998; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending December 31, 1997; Burn, G. [ed.] [comp.]; PB: 390 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Cr and Ti contents on the recovery, recrystallization, and mechanical properties of vanadium alloys
Tensile and impact properties of V-4Cr-4Ti alloy heats 832665 and 832864.
Fracture toughness testing of V-4Cr-4Ti at 25{degrees}C and -196{degrees}C
Technical Report
·
Mon Apr 01 00:00:00 EST 1996
·
OSTI ID:335381
+1 more
Tensile and impact properties of V-4Cr-4Ti alloy heats 832665 and 832864.
Conference
·
Mon Nov 08 00:00:00 EST 1999
·
OSTI ID:335381
+4 more
Fracture toughness testing of V-4Cr-4Ti at 25{degrees}C and -196{degrees}C
Technical Report
·
Tue Oct 01 00:00:00 EDT 1996
·
OSTI ID:335381