Nanostructured Alumina-Forming Austenitic Alloy (NAFA) Production Using Advanced Manufacturing

Technical Report · Sun Sep 01 04:00:00 EDT 2024

DOI:https://doi.org/10.2172/3002816· OSTI ID:3002816

Graening Seibert, Tim ^[1]; Massey, Caleb ^[1]; Hoelzer, David T. ^[1]; Yamamoto, Yukinori ^[1]; Hyer, Holden ^[1]; Kendall, Josh ^[1]; Yu, Xiao-Ying ^[1]; Parker, Gabriel ^[1]; Dryepondt, Sebastien ^[1]

---

1. Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)

Alumina-forming austenitic (AFA) alloys are well known for their exceptional corrosion-resistant properties due to the formation of a dense oxide scale beneficial in their application as a nuclear material. However, use of the alloys in core material applications is limited due to the high nickel-transmutation and helium generation rate in service, leading to swelling and reduced lifetimes. Enhancing the sink strength to pin gas bubbles and increasing gas management of the material may mitigate many of the degradation phenomena expected during alloy deployment (such as high-temperature helium embrittlement and cavity swelling for lead-cooled fast-reactor applications). Nanostructured materials are usually produced using a time-consuming and expensive batch process like mechanical alloying to achieve the fine homogenous distribution of nanoprecipitates throughout the matrix material. Integrating the nanoprecipitates in modern additive manufacturing processes has proven difficult, as the required nano-sizes or number densities cannot be achieved simultaneously. Efforts to increase the number density of precipitates by adding more precipitate-forming rare-earth elements led to agglomeration of such elements, while the nano-sized precipitates did not form in sufficient quantity when not enough rare-earth element was use. In this work a novel approach to advanced manufacturing and the fabrication of Nanostructured AFA (NAFA) materials was chosen. A dual precipitate-forming NAFA steel with a chemistry more suitable for advanced reactor applications was produced to create an environmentally resistant, high-sink-strength austenitic alloy for advanced reactor cladding applications.

• Research Organization: Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
• Sponsoring Organization: USDOE Office of Nuclear Energy (NE)
• DOE Contract Number: AC05-00OR22725
• OSTI ID: 3002816
• Report Number(s): ORNL/TM--2024/3606
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE