Study of the {alpha}{double_prime} phase texture obtained by martensitic {beta}-{alpha}{double_prime} phase transformation induced by tensile test in a sheet of Ti5Al2Sn4Zr4Mo2Cr1Fe
- Univ. de Metz (France). Lab. d`Etudes des Textures et Applications aux Materiaux
- Cezus, Ugine (France). Centre de Recherche
The purpose was to investigate the texture development of the {alpha}{double_prime} orthorhombic martensite phase induced by stress within a commercial sheet of Ti5Al2Sn4Zr4Mo2Cr1Fe. First, the experimental textures of the initial b.c.c. phase, then of the b.c.c. phase and the {alpha}{double_prime} martensite phase after a uniaxial deformation were determined from pole figures. Comparison of the {alpha}{double_prime} experimental texture with a {alpha}{double_prime} texture, simulated with no variant selection from the b.c.c. texture of the initial {beta} matrix clearly shows that a strong variant selection was induced by stress. In order to better understand the formation of this {alpha}{double_prime} orthorhombic texture, texture transformations were simulated according to different variant selection assumptions. As a result, it was shown that the {alpha}{double_prime} orthorhombic texture is formed by the variants favorably oriented with respect to stresses induced during tensile test.
- OSTI ID:
- 289507
- Journal Information:
- Acta Materialia, Journal Name: Acta Materialia Journal Issue: 16 Vol. 46; ISSN 1359-6454; ISSN ACMAFD
- Country of Publication:
- United States
- Language:
- English
Similar Records
A simple variant selection in stress-driven martensitic transformation
Modeling of the texture transformation in a Ti-64 sheet after hot compression