Effect of sulfate ions on corrosion inhibition of AA 7075 aluminum alloy in sodium chloride solutions
- Tatung Inst. of Tech., Taipei (Taiwan, Province of China). Dept. of Materials Engineering
- National Taiwan Ocean Univ., Keelung (Taiwan, Province of China). Inst. of Marine Materials Engineering
The effect of the addition of sulfate ions on corrosion inhibition of Aluminum Association (AA) 7075 aluminum (Al) alloy (UNS A97075) in aqueous solution was studied. Corrosion behavior was affected significantly by the addition of SO{sub 4}{sup 2{minus}}. The corrosion morphology and corrosion rate changed with various thermomechanical treatment sand with the relative amount of sodium sulfate and sodium chloride in the immersion test solutions. However, the inhibitive effect of SO{sub 4}{sup 2{minus}} was evident with the increasing relative amount of Na{sub 2}SO{sub 4}. Corrosion data and morphologies obtained were illustrated by a competitive anion adsorption mechanism.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 28021
- Journal Information:
- Corrosion, Vol. 51, Issue 3; Other Information: PBD: Mar 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion behavior of aluminum-lithium alloys
Boric/sulfuric acid anodizing of aluminum alloys 2024 and 7075: Film growth and corrosion resistance
Inhibition of corrosion of Al 6061, aluminum, and an aluminum-copper alloy in chloride-free aqueous media. Part 2: Behavior in basic solutions
Journal Article
·
Tue Mar 01 00:00:00 EST 1994
· Corrosion (Houston); (United States)
·
OSTI ID:28021
Boric/sulfuric acid anodizing of aluminum alloys 2024 and 7075: Film growth and corrosion resistance
Journal Article
·
Mon Nov 01 00:00:00 EST 1999
· Corrosion (Houston)
·
OSTI ID:28021
+1 more
Inhibition of corrosion of Al 6061, aluminum, and an aluminum-copper alloy in chloride-free aqueous media. Part 2: Behavior in basic solutions
Journal Article
·
Fri May 01 00:00:00 EDT 1998
· Corrosion
·
OSTI ID:28021