An elastic-plastic fracture mechanics analysis of weld-toe surface cracks in fillet welded T-butt joint
- British Gas plc, Newcastle upon Tyne (United Kingdom). Engineering Research Station
This paper describes an elastic-plastic fracture mechanics (EPFM) study of shallow weld-toe cracks. Two limiting crack configurations, plane strain edge crack and semi-circular surface crack in fillet welded T-butt plate joint, were analyzed using the finite element method. Crack depth ranging from 2 to 40% of plate thickness were considered. The elastic-plastic analysis, assuming power-law hardening relationship and Mises yield criterion, was based on incremental plasticity theory. Tension and bending loads applied were monotonically increased to a level causing relatively large scale yielding at the crack tip. Effects of weld-notch geometry and ductile material modeling on prediction of fracture mechanics characterizing parameter were assessed. It was found that the weld-notch effect reduces and the effect of material modeling increases as crack depth increases. Material modeling is less important than geometric modeling in analysis of very shallow cracks but is more important for relatively deeper cracks, e.g. crack depth more than 20% of thickness. The effect of material modeling can be assessed using a simplified structural model. Weld magnification factors derived assuming linear elastic conditions can be applied to EPFM characterization.
- OSTI ID:
- 27942
- Report Number(s):
- CONF-940230--; ISBN 0-7918-1266-9
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigation into the fatigue strength of fillet welded assemblies of E-36-4 steel as a function of the penetration of the weld subjected to tensile and bending loads
Reliability of welded structures containing fatigue cracks