High-resolution p-i-n CdTe and CdZnTe x-ray detectors with cooling and rise-time discrimination
- Metorex International Oy, Espoo (Finland)
- Baltic Scientific Instruments Ltd., Riga (Latvia)
The leakage current of CdTe detectors can be significantly reduced by processing detector crystals with p-i-n structures. Leakage currents of the order of several nA/mm{sup 2} are achieved at room temperature which compares well with the leakage current of commercially available CdZnTe detectors. The leakage current can be reduced further by cooling the detector to about {minus}30 C, where values of about pA/mm{sup 2} are achieved. These low values enable the use of low-noise, pulsed-optical feedback preamplifiers and higher bias voltages. High bias voltage is necessary for efficient charge collection which reduces spectrum background and peak tailing. Applying rise time discrimination circuitry to the linear amplifier reduces the tailing effect even further, especially at higher radiation energies. The authors tested several 4 to 30-mm{sup 2}, 0.6 to 1-mm thick p-i-n structure CdTe detector crystals at {minus}20 to {minus}30 C with a low-noise pulsed-optical feedback preamplifier and rise-time discriminator, and at best obtained energy resolutions of 700 eV at the 59.5-keV line of {sup 241}Am, 1.2 keV at the 122-keV line of {sup 57}Co, and 2.5 keV at the 662-keV line of {sup 137}Cs. A similar p-i-n structure was processed on a 4-mm{sup 2} Cd{sub 0.9}Zn{sub 0.1}Te detector crystal in order to reduce its leakage current, and energy resolutions of 368 eV at the 5.9-keV line of {sup 55}Fe, 670 eV at the 59.5-keV line of {sup 241}Am, and 2.6 keV at the 662-keV line of {sup 137}Cs were obtained. However, the detector suffered from a charge collection problem yielding relatively high background under the peaks.
- OSTI ID:
- 277703
- Report Number(s):
- CONF-951073--
- Journal Information:
- IEEE Transactions on Nuclear Science, Journal Name: IEEE Transactions on Nuclear Science Journal Issue: 3Pt2 Vol. 43; ISSN 0018-9499; ISSN IETNAE
- Country of Publication:
- United States
- Language:
- English
Similar Records
$gamma$-ray spectra detected with HgI$sub 2$ at room temperature
Fano factor determination for CZT