Effect of oxygen on the internal corrosion of natural gas pipelines
Book
·
OSTI ID:271982
- Cortest Columbus Technologies, Inc., Columbus, OH (United States)
Internal corrosion is a problem in wet natural gas gathering lines. Literature on the subject suggests that dissolved oxygen (O{sub 2}) is one of the more corrosive contaminants in natural gas. Immersion tests, funded by a major gas transmission company, were performed on C1018 (UNS G10180) specimens to assess the influence of O{sub 2} concentration on the internal corrosion of the wet gathering system in their storage field. Twenty-eight day tests were performed in a flow-through (gas phase only) autoclave at 70 F (21 C) and 1,200 psi (8,274 kPa) with simulated natural gas mixtures containing 10, 100, 500 and 1,000 ppm (by volume) O{sub 2}. Specimens were exposed to the vapor, vapor/liquid (V/L) interface, and liquid phases of pure water and saltwater in these tests. The highest corrosion rate, based on groove depth, was measured for the V/L specimens in pure water with 1,000 ppm O{sub 2}. Corrosion rates, based on weight loss, generally maximized at an O{sub 2} concentration of 100 ppm.
- OSTI ID:
- 271982
- Report Number(s):
- CONF-960389--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Carbon dioxide/hydrogen sulfide corrosion under wet low-flow gas pipeline conditions in the presence of bicarbonate, chloride, and oxygen. Final report
A CONTROLLED-ENVIRONMENT STEAM CORROSION FACILITY
AUTOCLAVE TESTING OF MONEL, NICKEL AND INCONEL
Technical Report
·
Sun Jun 01 00:00:00 EDT 1997
·
OSTI ID:325710
A CONTROLLED-ENVIRONMENT STEAM CORROSION FACILITY
Technical Report
·
Tue Oct 01 00:00:00 EDT 1963
·
OSTI ID:4127225
AUTOCLAVE TESTING OF MONEL, NICKEL AND INCONEL
Technical Report
·
Sun Oct 01 00:00:00 EDT 1961
·
OSTI ID:4813943