Laves phase in Ti-42Al-10Mn alloy
Journal Article
·
· Scripta Materialia
- Univ. of Birmingham (United Kingdom)
- Rolls-Royce plc, Derby (United Kingdom)
Mn is one of the most effective alloying additions to {gamma}-TiAl titanium aluminide for improving room temperature ductility. The purpose of this investigation as a whole is to study phase relationships in the Mn addition alloys over a wide range of temperatures and to determine the solubilities of Mn in the {gamma} and {alpha}{sub 2} phases in order to explore the potential of Mn additions to {gamma}-TiAl. The aim of this specific paper, however, is to confirm the identify of the ternary Ti{sub 3}Al{sub 3}Mn{sub 2} phase in the Ti-Al-Mn system and to show how to remove it.
- OSTI ID:
- 271643
- Journal Information:
- Scripta Materialia, Vol. 35, Issue 1; Other Information: PBD: 1 Jul 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tensile properties and fracture behavior of Ti[sub 52]Al[sub 48] and Ti[sub 50]Al[sub 48]Cr[sub 2] prepared from elemental powders
Phase relations in Ti-Al-Nb alloys at 1200 degrees C
Superplastic behavior in a two-phase TiAl alloy. [Ti-47. 3Al-1. 9Nb-1. 6Cr-0. 5Si-0. 4Mn]
Journal Article
·
Fri Oct 01 00:00:00 EDT 1993
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:271643
Phase relations in Ti-Al-Nb alloys at 1200 degrees C
Journal Article
·
Sun Mar 15 00:00:00 EST 1992
· Scripta Metallurgica; (United States)
·
OSTI ID:271643
Superplastic behavior in a two-phase TiAl alloy. [Ti-47. 3Al-1. 9Nb-1. 6Cr-0. 5Si-0. 4Mn]
Journal Article
·
Wed Dec 01 00:00:00 EST 1993
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:271643
+1 more