Fabrication of Iron-Containing Carbon Materials From Graphite Fluoride
Carbon materials containing iron alloy, iron metal, iron oxide or iron halide were fabricated. Typical samples of these metals were estimated to contain 1 iron atom per 3.5 to 5 carbon atoms. Those carbon materials containing iron alloy, iron metal, and/or Fe3O4 were magnetic. The kinetics of the fabrication process were studied by exposing graphite fluoride (CF(0.68)) to FeCl3 over a 280 to 420 C temperature range. Between 280 and 295 C, FeCl3 quickly entered the structure of CF(0.68), broke the carbon-fluorine bonds, and within 10 to 30 min, completely converted it to carbon made up of graphite planes between which particles of crystalline FeF3 and noncrystalline FeCl3 were located. Longer reaction times (e.g., 28 hr) or higher reaction temperatures (e.g., 420 C) produced materials containing graphite, a FeCl3-graphite intercalation compound, FeCl2(center dot)4H2O, and FeCl2(center dot)2H2O. These products were further heat treated to produce iron-containing carbon materials. When the heating temperature was kept in the 750 to 850 C range, and the oxygen supply was kept at the optimum level, the iron halides in the carbon structure were converted to iron oxides. Raising the heat to temperatures higher than 900 C reduced such iron oxides to iron metal. The kinetics of these reactions were used to suggest processes for fabricating carbon materials containing iron alloy. Such processes were then tested experimentally. In one of the successful trial runs, commercially purchased CF(0.7) powder was used as the reactant, and NiO was added during the final heating to 1200 C as a source of both nickel and oxygen. The product thus obtained was magnetic and was confirmed to be a nickel-iron alloy in carbon.
- Research Organization:
- NASA Lewis Research Center, Cleveland, OH (United States)
- OSTI ID:
- 263848
- Report Number(s):
- N-96-24050; NASA-TM-107133; E-10063; NAS-1.15:107133; NIPS-96-43626; CONF-9507143-; TRN: 9624050
- Resource Relation:
- Conference: 22. biennial conference on carbon, San Diego, CA (United States), 16-21 Jul 1995; Other Information: PBD: Apr 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetic properties of iron-bearing graphite fibers
METALLURGY DIVISION QUARTERLY PROGRESS REPORT FOR PERIOD ENDING OCTOBER 31, 1951