Creep and corrosion-resistant cast alumina-forming alloys for high temperature service in industrial and petrochemical applications

Patent · Tue Jan 09 04:00:00 EST 2024

OSTI ID:2541656

Muralidharan, Govindarajan; Brady, Michael P.; Yamamoto, Yukinori

An austenitic Ni-base alloy, consisting essentially of, in weight percent: 2.5 to 4.75 Al; 21 to 26 Cr; 20 to 40 Fe; 0.75 to 2.5 total of at least one element elected from the group consisting of Nb and Ta; 0 to 0.25 Ti; 0.09 to 1.5 Si; 0 to 0.5 V; 0 to 2 Mn; 0 to 3 Cu; 0 to 2 of at least one element selected from the group consisting of Mo and W; 0 to 1 of at least one element selected from the group consisting of Zr and Hf; 0 to 0.15 Y; 0.3 to 0.55 C; 0.005 to 0.1 B; 0 to 0.05 P; less than 0.06 N and balance Ni (30 to 46 Ni), wherein the weight percent Ni is greater than the weight percent Fe, and wherein the ratio Ni/(Fe+2*C) is between 1.02 and 1.067.

• Research Organization: Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
• Sponsoring Organization: USDOE
• DOE Contract Number: AC05-00OR22725
• Assignee: UT-Battelle, LLC (Oak Ridge, TN)
• Patent Number(s): 11,866,809
• Application Number: 17/162,917
• OSTI ID: 2541656
• Country of Publication: United States
• Language: English