High strain rate deformation of Ti-48Al-2Nb-2Cr
Journal Article
·
· Acta Materialia
- Los Alamos National Lab., NM (United States)
The compressive deformation behavior of Ti-48Al-2NB-2Cr in the duplex microstructural morphology has been studied at strain rates of 0.001 and 2,000 s{sup {minus}1} over the temperature range from {minus}196 to 1,100 C. The yield stress for the duplex microstructure is strain rate sensitive at 25 C and increases with temperature from 500 to 1,100 C at a strain rate of 2,000 s{sup {minus}1}. TEM investigations revealed that deformation occurs in {gamma}-TiAl by means of {l_brace}111{r_brace}<112> twinning, 1/2<110> slip and <101> superdislocations under all conditions depending on the orientation of the grain with respect to the deformation axis. Optical metallography revealed that twinning increases with increasing strain rate. The flow stress anomaly is discussed in reference to the dislocation substructure in {gamma}-TiAl.
- OSTI ID:
- 247934
- Journal Information:
- Acta Materialia, Journal Name: Acta Materialia Journal Issue: 5 Vol. 44; ISSN XZ504Y; ISSN 1359-6454
- Country of Publication:
- United States
- Language:
- English
Similar Records
High strain rate deformation of Ti-48Al-2Cr-2Nb in the duplex morphology
Effects of processing variables on the creep behavior of investment cast Ti-48Al-2Nb-2Cr
The hot workability and superplasticity of Ti-48Al-2Nb-2Cr alloys
Conference
·
Tue Feb 28 23:00:00 EST 1995
·
OSTI ID:70757
Effects of processing variables on the creep behavior of investment cast Ti-48Al-2Nb-2Cr
Book
·
Sat Dec 30 23:00:00 EST 1995
·
OSTI ID:225117
The hot workability and superplasticity of Ti-48Al-2Nb-2Cr alloys
Technical Report
·
Sat Jan 31 23:00:00 EST 1998
·
OSTI ID:329558