Platinum and CeO 2-x Occlusion Electrodeposition at Unsupported Vulcan XC-72R for Methanol and Ethanol Oxidation Reactions in Alkaline Media
Abstract
Platinum was electrodeposited in a slurry solution of CeO2 and Vulcan XC-72R to produce Pt/CeO2-x/Vulcan XC-72R catalysts by using the Rotating Disk Slurry Electrodeposition (RoDSE) Technique. The activity of the catalysts was measured towards methanol and ethanol oxidation reactions in alkaline conditions by cyclic voltammetry and chronoamperometry. The electrochemical results were compared to those obtained on commercial catalysts. Pt/CeO2-x/Vulcan XC-72R (with ~ 26 wt.% Pt) catalyst was the most active for both alcohol oxidation reactions when compared to commercial 40 wt.% and 20% /Vulcan XC-72R (ETEK) catalysts. The mass activity increases 2.0x and 2.4x for methanol and ethanol oxidation reactions when compare with 40 and 20 Pt wt. % commercial catalysts, respectively. The Pt/CeO2-x/Vulcan XC-72R catalysts contained Pt nanoparticles growth within the cerium oxide through an occlusion electrodeposition method. These effects were systematically investigated using X-ray Diffraction (XRD), High Resolution Transmission Electron Microscopy (HR-TEM), and X-ray Photoelectron Spectroscopy (XPS).
- Sponsoring Organization:
- USDOE
- Grant/Contract Number:
- NONE; SC0019445
- OSTI ID:
- 2446746
- Journal Information:
- ECS Advances, Journal Name: ECS Advances; ISSN 2754-2734
- Publisher:
- The Electrochemical SocietyCopyright Statement
- Country of Publication:
- United Kingdom
- Language:
- English
Similar Records
Rotating Disk Slurry Au Electrodeposition at Unsupported Carbon Vulcan XC-72 and Ce3+ Impregnation for Ethanol Oxidation in Alkaline Media
Combined Rotating Disk Slurry Electrodeposition–Spontaneous Galvanic Displacement for Pt-M (M = Co, Ni, and Cu) Catalyst Synthesis for the Oxygen Reduction Reaction in Alkaline Media