EPMA on interfaces between cathode and electrolyte of the solid oxide fuel cell
Book
·
OSTI ID:242555
- Research Centre Juelich (Germany). Inst. for Materials in Energy Systems
The interface of La{sub y{minus}x}Sr{sub x}MnO{sub 3}/YSZ was studied with EPMA after annealing at 1200 C to 1400 C for various times. Typical reaction products (Zirconates) and a diffusion zone of Mn and La in the YSZ were determined using quantitative microanalysis. The chemical reactivity at the interface is dependent on the stoichiometry (y) and the Sr content (x) of the perovskite. An increased Sr content leads to a decreased formation of La{sub 2}Zr{sub 2}O{sub 7} but also to an increased diffusion of Mn oxide into the electrolyte material. A high Sr content (x=0.4) reveals both aspects: the formation of a La- and Mn-enriched SrZrO{sub 3} layer at the reaction interface, as well as a diffusion of Mn oxide into YSZ.
- OSTI ID:
- 242555
- Report Number(s):
- CONF-950683--; ISBN 1-56677-095-5
- Country of Publication:
- United States
- Language:
- English
Similar Records
SrZrO3 Formation at the Interlayer/Electrolyte Interface during (La1-xSrx)1-δCo1-yFeyO3 Cathode Sintering
Chemical compatibility between strontium-doped lanthanum manganite and yttria-stabilized zirconia
Mechanism of reaction between lanthanum manganite and yttria-stabilized zirconia
Journal Article
·
Tue Jul 18 20:00:00 EDT 2017
· Journal of the Electrochemical Society
·
OSTI ID:1390433
Chemical compatibility between strontium-doped lanthanum manganite and yttria-stabilized zirconia
Journal Article
·
Fri Mar 31 23:00:00 EST 1995
· Journal of the American Ceramic Society
·
OSTI ID:82585
Mechanism of reaction between lanthanum manganite and yttria-stabilized zirconia
Journal Article
·
Fri Jan 31 23:00:00 EST 1992
· Journal of the American Ceramic Society; (United States)
·
OSTI ID:5527139
Related Subjects
30 DIRECT ENERGY CONVERSION
ACTIVATION ENERGY
CATHODES
ELECTRON MICROPROBE ANALYSIS
EXPERIMENTAL DATA
HEAT TREATMENTS
INTERFACES
LANTHANUM OXIDES
MANGANESE OXIDES
MASS TRANSFER
METALLURGICAL EFFECTS
SOLID ELECTROLYTE FUEL CELLS
SOLID ELECTROLYTES
SOLUBILITY
STRONTIUM
STRONTIUM OXIDES
YTTRIUM OXIDES
ZIRCONIUM OXIDES
ACTIVATION ENERGY
CATHODES
ELECTRON MICROPROBE ANALYSIS
EXPERIMENTAL DATA
HEAT TREATMENTS
INTERFACES
LANTHANUM OXIDES
MANGANESE OXIDES
MASS TRANSFER
METALLURGICAL EFFECTS
SOLID ELECTROLYTE FUEL CELLS
SOLID ELECTROLYTES
SOLUBILITY
STRONTIUM
STRONTIUM OXIDES
YTTRIUM OXIDES
ZIRCONIUM OXIDES