Role of Tartaric Acid in Chemical, Mechanical and Self-Healing Behaviors of a Calcium-Aluminate Cement Blend with Fly Ash F under Steam and Alkali Carbonate Environments at 270 °C
Tartaric acid (TA) changes short-term mechanical behavior and phase composition of sodium-metasilicate activated calcium-aluminate cement blend with fly ash, type F, when used as a set control additive to allow sufficient pumping time for underground well placement. The present work focuses on TA effect on self-healing properties of the blend under steam or alkali carbonate environments at 270 °C applicable to geothermal wells. Compressive strength recoveries and cracks sealing were examined to evaluate self-healing of the cement after repeated crush tests followed by two consecutive healing periods of 10 and 5 days at 270 °C. Optical and scanning electron microscopes, X-ray diffraction, Fourier Transform infrared and EDX measurements along with thermal gravimetric analyses were used to identify phases participating in the healing processes. Samples with 1% mass fraction of TA by weight of blend demonstrated improved strength recoveries and crack plugging properties, especially in alkali carbonate environment. This effect was attributed to silicon-rich (C,N)-A-S-H amorphous phase predominant in TA-modified samples, high-temperature stable zeolite phases along with the formation of tobermorite-type crystals in the presence of tartaric acid.
Pyatina, Tatiana and Sugama, Toshifumi. "Role of Tartaric Acid in Chemical, Mechanical and Self-Healing Behaviors of a Calcium-Aluminate Cement Blend with Fly Ash F under Steam and Alkali Carbonate Environments at 270 °C." Materials, vol. 10, no. 4, Mar. 2017. https://doi.org/10.3390/ma10040342
Pyatina, Tatiana, & Sugama, Toshifumi (2017). Role of Tartaric Acid in Chemical, Mechanical and Self-Healing Behaviors of a Calcium-Aluminate Cement Blend with Fly Ash F under Steam and Alkali Carbonate Environments at 270 °C. Materials, 10(4). https://doi.org/10.3390/ma10040342
Pyatina, Tatiana, and Sugama, Toshifumi, "Role of Tartaric Acid in Chemical, Mechanical and Self-Healing Behaviors of a Calcium-Aluminate Cement Blend with Fly Ash F under Steam and Alkali Carbonate Environments at 270 °C," Materials 10, no. 4 (2017), https://doi.org/10.3390/ma10040342
@article{osti_2371065,
author = {Pyatina, Tatiana and Sugama, Toshifumi},
title = {Role of Tartaric Acid in Chemical, Mechanical and Self-Healing Behaviors of a Calcium-Aluminate Cement Blend with Fly Ash F under Steam and Alkali Carbonate Environments at 270 °C},
annote = {Tartaric acid (TA) changes short-term mechanical behavior and phase composition of sodium-metasilicate activated calcium-aluminate cement blend with fly ash, type F, when used as a set control additive to allow sufficient pumping time for underground well placement. The present work focuses on TA effect on self-healing properties of the blend under steam or alkali carbonate environments at 270 °C applicable to geothermal wells. Compressive strength recoveries and cracks sealing were examined to evaluate self-healing of the cement after repeated crush tests followed by two consecutive healing periods of 10 and 5 days at 270 °C. Optical and scanning electron microscopes, X-ray diffraction, Fourier Transform infrared and EDX measurements along with thermal gravimetric analyses were used to identify phases participating in the healing processes. Samples with 1% mass fraction of TA by weight of blend demonstrated improved strength recoveries and crack plugging properties, especially in alkali carbonate environment. This effect was attributed to silicon-rich (C,N)-A-S-H amorphous phase predominant in TA-modified samples, high-temperature stable zeolite phases along with the formation of tobermorite-type crystals in the presence of tartaric acid.},
doi = {10.3390/ma10040342},
url = {https://www.osti.gov/biblio/2371065},
journal = {Materials},
issn = {ISSN MATEG9},
number = {4},
volume = {10},
place = {Switzerland},
publisher = {MDPI AG},
year = {2017},
month = {03}}