Towards understanding stress corrosion cracking of austenitic stainless steels exposed to realistic sea salt brines

Katona, R. M.; Taylor, J. M.; McCready, T. A.; Bryan, C. R.; Schaller, R. F.

doi:10.1016/j.corsci.2024.111992

Towards understanding stress corrosion cracking of austenitic stainless steels exposed to realistic sea salt brines

Journal Article · Wed May 01 00:00:00 EDT 2024 · Corrosion Science

DOI:https://doi.org/10.1016/j.corsci.2024.111992· OSTI ID:2331333

Katona, R. M.; Taylor, J. M.; McCready, T. A.; Bryan, C. R.; Schaller, R. F.

Not Available

View Journal Article

Sponsoring Organization:: USDOE National Nuclear Security Administration (NNSA)

Grant/Contract Number:: NA0003525

OSTI ID:: 2331333

Journal Information:: Corrosion Science, Journal Name: Corrosion Science Journal Issue: C Vol. 232; ISSN 0010-938X

Publisher:: ElsevierCopyright Statement

Country of Publication:: United Kingdom

Language:: English

References (78)

SCC Testing and Data Quality Considerations Andresen, Peter L. Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors https://doi.org/10.1002/9781118787618.ch42	other	August 1999
On the calibration of the electrical potential technique for monitoring crack growth using finite element methods Ritchie, R. O.; Bathe, K. J. International Journal of Fracture, Vol. 15, Issue 1 https://doi.org/10.1007/BF00115908	journal	February 1979
The threshold stress intensity for hydrogen-induced crack growth Akhurst, K. N.; Baker, T. J. Metallurgical Transactions A, Vol. 12, Issue 6 https://doi.org/10.1007/BF02643487	journal	June 1981
Stress corrosion cracking of stainless steels in NaCl solutions Speidel, Markus O. Metallurgical Transactions A, Vol. 12, Issue 5 https://doi.org/10.1007/BF02648342	journal	May 1981
A mechanistic study of transgranular stress corrosion cracking of type 304 stainless steel Jani, S.; Marek, M.; Hochman, R. F. Metallurgical Transactions A, Vol. 22, Issue 6 https://doi.org/10.1007/BF02660677	journal	June 1991
Measurement and Modeling of Hydrogen Environment-Assisted Cracking in Monel K-500 Gangloff, Richard P.; Ha, Hung M.; Burns, James T. Metallurgical and Materials Transactions A, Vol. 45, Issue 9 https://doi.org/10.1007/s11661-014-2324-z	journal	May 2014
The Effect of Microstructural Variation on the Hydrogen Environment-Assisted Cracking of Monel K-500 Harris, Zachary D.; Dolph, Justin D.; Pioszak, Greger L. Metallurgical and Materials Transactions A, Vol. 47, Issue 7 https://doi.org/10.1007/s11661-016-3486-7	journal	April 2016
Effect of Strain Rate on Stress Corrosion Cracking of 316L Austenitic Stainless Steel in Boiling MgCl2 Environment Hassani, A.; Habibolahzadeh, A.; Javadi, A. H. Journal of Materials Engineering and Performance, Vol. 22, Issue 6 https://doi.org/10.1007/s11665-012-0461-3	journal	December 2012
Stress corrosion cracking of cold-worked austenitic stainless steels Cigada, A.; Mazza, B.; Pedeferri, P. Corrosion Science, Vol. 22, Issue 6 https://doi.org/10.1016/0010-938X(82)90055-5	journal	January 1982
A coupled environment model for stress corrosion cracking in sensitized type 304 stainless steel in LWR environments MacDonald, Digby D.; Urquidi-MacDonald, Mirna Corrosion Science, Vol. 32, Issue 1 https://doi.org/10.1016/0010-938X(91)90063-U	journal	January 1991
Discussion on “Determination of the fate of the current in the SCC of sensitized type 304 SS in high temperature aqueous systems” Andresen, Peter L. Corrosion Science, Vol. 37, Issue 12 https://doi.org/10.1016/0010-938X(95)99261-X	journal	December 1995
Response to “ On the modeling of stress corrosion cracking of iron and nickel base alloys in high temperature aqueous environments” Andresen, Peter L.; Ford, F. Peter Corrosion Science, Vol. 38, Issue 6 https://doi.org/10.1016/0010-938X(96)00055-8	journal	June 1996
On the relationship between critical tensile stress and fracture toughness in mild steel Ritchie, R. O.; Knott, J. F.; Rice, J. R. Journal of the Mechanics and Physics of Solids, Vol. 21, Issue 6 https://doi.org/10.1016/0022-5096(73)90008-2	journal	November 1973
Life prediction by mechanistic modeling and system monitoring of environmental cracking of iron and nickel alloys in aqueous systems Andresen, Peter L.; Peter Ford, F. Materials Science and Engineering: A, Vol. 103, Issue 1 https://doi.org/10.1016/0025-5416(88)90564-2	journal	August 1988
Clarification of issues raised by P.L. Andresen and F.P. Ford in their response to “On the modeling of stress corrosion cracking of iron and nickel base alloys in high temperature aqueous environments” Macdonald, D. D. Corrosion Science, Vol. 39, Issue 8 https://doi.org/10.1016/S0010-938X(97)00042-5	journal	August 1997
Modelling of crack chemistry in sensitized stainless steel in boiling water reactor environments Turnbull, A. Corrosion Science, Vol. 39, Issue 4 https://doi.org/10.1016/S0010-938X(97)89342-0	journal	April 1997
Using capillary electrophoresis to study the chemical conditions within cracks in aluminum alloys Cooper, K. R.; Kelly, R. G. Journal of Chromatography A, Vol. 850, Issue 1-2 https://doi.org/10.1016/S0021-9673(99)00317-9	journal	July 1999
Theoretical and experimental study on the temperature distribution of H-shaped steel members under solar radiation Liu, Hongbo; Chen, Zhihua; Zhou, Ting Applied Thermal Engineering, Vol. 37 https://doi.org/10.1016/j.applthermaleng.2011.11.045	journal	May 2012
Experimental and numerical investigation of temperature effects on steel members due to solar radiation Chen, Deshen; Wang, Huajie; Qian, Hongliang Applied Thermal Engineering, Vol. 127 https://doi.org/10.1016/j.applthermaleng.2017.08.045	journal	December 2017
The effect of test temperature on SCC behavior of austenitic stainless steels in boiling saturated magnesium chloride solution Alyousif, Osama M.; Nishimura, Rokuro Corrosion Science, Vol. 48, Issue 12 https://doi.org/10.1016/j.corsci.2006.01.014	journal	December 2006
Crack tip chemistry and electrochemistry of environmental cracks in AA 7050 Cooper, Kevin R.; Kelly, R. G. Corrosion Science, Vol. 49, Issue 6 https://doi.org/10.1016/j.corsci.2006.12.001	journal	June 2007
The stress corrosion cracking behavior of austenitic stainless steels in boiling magnesium chloride solutions Alyousif, Osama M.; Nishimura, Rokuro Corrosion Science, Vol. 49, Issue 7 https://doi.org/10.1016/j.corsci.2006.12.023	journal	July 2007
Film rupture model for aqueous stress corrosion cracking under constant and variable stress intensity factor Hall, M. M. Corrosion Science, Vol. 51, Issue 2 https://doi.org/10.1016/j.corsci.2008.08.052	journal	February 2009
Critique of the Ford–Andresen film rupture model for aqueous stress corrosion cracking Hall, M. M. Corrosion Science, Vol. 51, Issue 5 https://doi.org/10.1016/j.corsci.2009.02.022	journal	May 2009
Experimental and numerical investigation of stress corrosion cracking of sensitized type 304 stainless steel under high-temperature and high-purity water Fujii, Tomoyuki; Tohgo, Keiichiro; Kenmochi, Akihiro Corrosion Science, Vol. 97 https://doi.org/10.1016/j.corsci.2015.05.001	journal	August 2015
Effect of machining-induced surface residual stress on initiation of stress corrosion cracking in 316 austenitic stainless steel Zhang, Wenqian; Fang, Kewei; Hu, Yujin Corrosion Science, Vol. 108 https://doi.org/10.1016/j.corsci.2016.03.008	journal	July 2016
On the stress corrosion crack growth behaviour in high temperature water of 316L stainless steel made by laser powder bed fusion additive manufacturing Lou, Xiaoyuan; Song, Miao; Emigh, Paul W. Corrosion Science, Vol. 128 https://doi.org/10.1016/j.corsci.2017.09.017	journal	November 2017
Importance of the hydrogen evolution reaction in magnesium chloride solutions on stainless steel Katona, R. M.; Carpenter, J. C.; Knight, A. W. Corrosion Science, Vol. 177 https://doi.org/10.1016/j.corsci.2020.108935	journal	December 2020
Atmospheric stress corrosion crack growth rates of 316 L stainless steel for nuclear waste containment Zhang, Y.; Cook, A. J. M. C.; Padovani, C. Corrosion Science, Vol. 177 https://doi.org/10.1016/j.corsci.2020.109008	journal	December 2020
On the loading rate dependence of environment-assisted cracking in sensitized AA5456-H116 exposed to marine environments Harris, Zachary D.; Burns, James T. Corrosion Science, Vol. 201 https://doi.org/10.1016/j.corsci.2022.110267	journal	June 2022
Insights from electrochemical crack tip modeling of atmospheric stress corrosion cracking Katona, R. M.; Burns, J. T.; Schaller, R. F. Corrosion Science, Vol. 209 https://doi.org/10.1016/j.corsci.2022.110756	journal	December 2022
Spatial determination of diffusible hydrogen concentrations proximate to pits in a Fe–Cr–Ni–Mo steel using the Scanning Kelvin Probe Schaller, R. F.; Scully, J. R. Electrochemistry Communications, Vol. 63 https://doi.org/10.1016/j.elecom.2015.12.002	journal	February 2016
Pitting and stress corrosion cracking behavior in welded austenitic stainless steel Lu, B. T.; Chen, Z. K.; Luo, J. L. Electrochimica Acta, Vol. 50, Issue 6 https://doi.org/10.1016/j.electacta.2004.08.036	journal	January 2005
Nitrate on localized corrosion of carbon steel and stainless steel in aqueous solutions Xu, Weichen; Zhang, Binbin; Deng, Yu Electrochimica Acta, Vol. 369 https://doi.org/10.1016/j.electacta.2020.137660	journal	February 2021
Predicting the influence of strain on crack length measurements performed using the potential drop method Tarnowski, K. M.; Dean, D. W.; Nikbin, K. M. Engineering Fracture Mechanics, Vol. 182 https://doi.org/10.1016/j.engfracmech.2017.06.008	journal	September 2017
Effect of microstructural and environmental variables on ductility of austenitic stainless steels San Marchi, C.; Ronevich, J. A.; Sabisch, J. E. C. International Journal of Hydrogen Energy, Vol. 46, Issue 23 https://doi.org/10.1016/j.ijhydene.2020.09.069	journal	March 2021
Development of a fundamental crack tip strain rate equation and its application to quantitative prediction of stress corrosion cracking of stainless steels in high temperature oxygenated water Peng, Q. J.; Kwon, J.; Shoji, T. Journal of Nuclear Materials, Vol. 324, Issue 1 https://doi.org/10.1016/j.jnucmat.2003.09.008	journal	January 2004
Corrosion and stress corrosion cracking in supercritical water Was, G. S.; Ampornrat, P.; Gupta, G. Journal of Nuclear Materials, Vol. 371, Issue 1-3 https://doi.org/10.1016/j.jnucmat.2007.05.017	journal	September 2007
Microstructural changes in AISI 304L stainless steel due to surface machining: Effect on its susceptibility to chloride stress corrosion cracking Ghosh, Swati; Kain, Vivekanand Journal of Nuclear Materials, Vol. 403, Issue 1-3 https://doi.org/10.1016/j.jnucmat.2010.05.028	journal	August 2010
dK/da effects on the SCC growth rates of nickel base alloys in high-temperature water Chen, Kai; Wang, Jiamei; Du, Donghai Journal of Nuclear Materials, Vol. 503 https://doi.org/10.1016/j.jnucmat.2018.02.032	journal	May 2018
Role of residual stresses induced by industrial fabrication on stress corrosion cracking susceptibility of austenitic stainless steel Ghosh, Swati; Rana, Vishav Preet Singh; Kain, Vivekanand Materials & Design, Vol. 32, Issue 7 https://doi.org/10.1016/j.matdes.2011.03.012	journal	August 2011
Physical and chemical properties of sea salt deliquescent brines as a function of temperature and relative humidity Bryan, C. R.; Knight, A. W.; Katona, R. M. Science of The Total Environment, Vol. 824 https://doi.org/10.1016/j.scitotenv.2022.154462	journal	June 2022
Chemical and electrochemical conditions within stress corrosion and corrosion fatigue cracks Bland, Leslie G.; Locke, Jenifer S. npj Materials Degradation, Vol. 1, Issue 1 https://doi.org/10.1038/s41529-017-0015-0	journal	October 2017
Crystallographic effects on transgranular chloride-induced stress corrosion crack propagation of arc welded austenitic stainless steel Qu, Haozheng J.; Tao, Fei; Gu, Nianju npj Materials Degradation, Vol. 6, Issue 1 https://doi.org/10.1038/s41529-022-00252-2	journal	May 2022
Application of Fracture Mechanics Techniques to the Environmentally Assisted Cracking of Aluminium 2024 Dietzel, W.; Schwalbe, K. ‐H.; Wu, D. Fatigue & Fracture of Engineering Materials & Structures, Vol. 12, Issue 6 https://doi.org/10.1111/j.1460-2695.1989.tb00559.x	journal	November 1989
Effect of Rising and Falling K Profiles on SCC Growth Rates in High-Temperature Water Andresen, Peter L.; Morra, Martin M. Journal of Pressure Vessel Technology, Vol. 129, Issue 3 https://doi.org/10.1115/1.2748830	journal	November 2006
Pitting Corrosion of Metals Frankel, G. S. Journal of The Electrochemical Society, Vol. 145, Issue 6 https://doi.org/10.1149/1.1838615	journal	January 1998
Long-Term Effects of Humidity on Stainless Steel Pitting in Sea Salt Exposures Srinivasan, J.; Weirich, T. D.; Marino, G. A. Journal of The Electrochemical Society, Vol. 168, Issue 2 https://doi.org/10.1149/1945-7111/abdc75	journal	February 2021
Influence of Realistic, Cyclic Atmospheric Cycles on the Pitting Corrosion of Austenitic Stainless Steels Montoya, T.; Katona, R. M.; Karasz, E. K. Journal of The Electrochemical Society, Vol. 170, Issue 4 https://doi.org/10.1149/1945-7111/acc42e	journal	April 2023
Oxygen Reduction on Stainless Steel in Concentrated Chloride Media Alexander, Christopher L.; Liu, Chao; Alshanoon, Ali Journal of The Electrochemical Society, Vol. 165, Issue 13 https://doi.org/10.1149/2.0181813jes	journal	January 2018
Humidity Effects on Pitting of Ground Stainless Steel Exposed to Sea Salt Particles Weirich, Timothy D.; Srinivasan, Jayendran; Taylor, Jason M. Journal of The Electrochemical Society, Vol. 166, Issue 11 https://doi.org/10.1149/2.0551911jes	journal	January 2019
Effect of Nitrate and Sulfate on Atmospheric Corrosion of 304L and 316L Stainless Steels Cook, Angus J. M. C.; Padovani, Cristiano; Davenport, Alison J. Journal of The Electrochemical Society, Vol. 164, Issue 4 https://doi.org/10.1149/2.0921704jes	journal	January 2017
Evaluating Localized Corrosion Susceptibility of Austenitic Stainless Steels Exposed to Varying Nitrate to Chloride Ratio Droplets Katona, Ryan Michael; Montoya, Timothy; Snow, Jason ECS Meeting Abstracts, Vol. MA2022-02, Issue 12 https://doi.org/10.1149/MA2022-0212773mtgabs	journal	October 2022
Effect of Atmospheric Conditions on Galvanic Corrosion and Environmental Cracking of an Aerospace Aluminum Alloy Agnew, Liam; Clark, Brandi; Brown, Nathan Advances in Accelerated Testing and Predictive Methods in Creep, Fatigue, and Environmental Cracking https://doi.org/10.1520/STP164320210055	book	May 2023
Gap Analysis to Guide DOE R&D in Supporting Extended Storage and Transportation of Spent Nuclear Fuel: An FY2019 Assessment (Final Report) Teague, Melissa; Saltzstein, Sylvia; Hanson, Brady https://doi.org/10.2172/1592862	report	December 2019
FY21 Status Report: Probabilistic SCC Model for SNF Dry Storage Canisters Porter, Nathan; Brooks, Dusty; Bryan, Charles https://doi.org/10.2172/1822281	report	July 2021
SNF Interim Storage Canister Corrosion and Surface Environment Investigations (FY21 Status Report) Bryan, Charles; Knight, Andrew; Nation, Brendan https://doi.org/10.2172/1825847	report	September 2021
Stress Corrosion Cracking of Austenitic Stainless Steels: Correlating in-situ crack tip chemistry and crack growth rate measurements. Katona, Ryan; Taylor, Jason; Bryan, Charles Proposed for presentation at the AMPP Annual Conference in , https://doi.org/10.2172/2005637	conference	October 2022
Engineering approach for elastic-plastic fracture analysis Kumar, V.; German, M. D.; Shih, C. F. https://doi.org/10.2172/6068291	report	July 1981
Stress Corrosion Cracking Growth Rates of Candidate Canister Materials for Spent Nuclear Fuel Storage in Chloride-Containing Atmosphere Tani, Jun-ichi; Mayuzumi, Masami; Arai, Taku MATERIALS TRANSACTIONS, Vol. 48, Issue 6 https://doi.org/10.2320/matertrans.MRA2006367	journal	January 2007
The Effect of Loading Rate on the Environment-Assisted Cracking Behavior of AA7075-T651 in Aqueous NaCl Solution Harris, Zachary D.; Burns, James T. Corrosion and Materials Degradation, Vol. 2, Issue 3 https://doi.org/10.3390/cmd2030019	journal	July 2021
The Effect of Cold Work on the Stress-Corrosion Cracking of Type 302 Austenitic Stainless Steel Greeley, P. J.; Russo, V. J.; Saxer, R. K. Corrosion, Vol. 21, Issue 10 https://doi.org/10.5006/0010-9312-21.10.327	journal	October 1965
Mechanism of Chloride Stress Corrosion Cracking of Austenitic Stainless Steels Rhodes, P. R. Corrosion, Vol. 25, Issue 11 https://doi.org/10.5006/0010-9312-25.11.462	journal	November 1969
Stress Corrosion Crack Growth in Austenitic Stainless Steel Speidel, Markus O. Corrosion, Vol. 33, Issue 6 https://doi.org/10.5006/0010-9312-33.6.199	journal	June 1977
Effect of Loading Rate on Environmentally Controlled Cracking of Sensitized 304 Stainless Steel in High Purity Water Ford, F. P.; Silverman, M. CORROSION, Vol. 36, Issue 11 https://doi.org/10.5006/0010-9312-36.11.597	journal	November 1980
Stress Corrosion Crack Growth in Type 316 Stainless Steel in Supercritical Water Peng, Q. J.; Teysseyre, S.; Andresen, P. L. CORROSION, Vol. 63, Issue 11 https://doi.org/10.5006/1.3278318	journal	November 2007
Emerging Issues and Fundamental Processes in Environmental Cracking in Hot Water Andresen, P. L. CORROSION, Vol. 64, Issue 5 https://doi.org/10.5006/1.3278483	journal	May 2008
Effects of Temperature on Crack Growth Rate in Sensitized Type 304 Stainless Steel and Alloy 600 Andresen, P. L. CORROSION, Vol. 49, Issue 9 https://doi.org/10.5006/1.3316104	journal	September 1993
Influence of Nitrate on Pit Stability in Austenitic Stainless Steel Lillard, R. S.; Vasquez, G.; Bahr, D. F. CORROSION, Vol. 66, Issue 7 https://doi.org/10.5006/1.3462911	journal	July 2010
Intergranular Stress Corrosion Cracking of Austenitic Stainless Steel at Temperatures Below 100 C — A Review Cragnolino, G.; Macdonald, D. D. Corrosion, Vol. 38, Issue 8 https://doi.org/10.5006/1.3577354	journal	August 1982
Effects of Transients in Water Chemistry, Temperature, and Loading on Intergranular Stress Corrosion Cracking of AISI 304 Stainless Steel Andresen, P. L. CORROSION, Vol. 42, Issue 3 https://doi.org/10.5006/1.3584898	journal	March 1986
Probabilistic Fracture Mechanics Simulation of Stress Corrosion Cracking Using Accelerated Laboratory Testing and Multi-Scale Modeling Gangloff, Richard P. Corrosion, Vol. 72, Issue 7 https://doi.org/10.5006/1920	journal	July 2016
Stress Corrosion Cracking and Localized Corrosion of Carbon Steel in Nitrate Solutions Sridhar, N.; Beavers, J. A.; Rollins, B. Corrosion, Vol. 72, Issue 7 https://doi.org/10.5006/2035	journal	July 2016
Mechanistic Studies of Intergranular Stress Corrosion Cracking in Al-Mg Alloys under Atmospheric Exposure Conditions Steiner, P. J.; Burns, J. T. Corrosion, Vol. 74, Issue 10 https://doi.org/10.5006/2853	journal	July 2018
A Brief History of Environmental Cracking in Hot Water Andresen, Peter L. CORROSION, Vol. 75, Issue 3 https://doi.org/10.5006/2881	journal	July 2018
Atmospheric Stress Corrosion Cracking of Stainless Steel Rock Climbing Anchors, Part 2: Laboratory Experiments Prošek, Tomáš; Lieberzeit, Jiří; Jarvis, Alan CORROSION, Vol. 75, Issue 11 https://doi.org/10.5006/3242	journal	August 2019
Investigation of IG-SCC Growth Kinetics in Al-Mg Alloys in Thin Film Environments Steiner, Patrick J.; Harris, Zachary D.; Moraes, Carolina Vicente Corrosion, Vol. 77, Issue 8 https://doi.org/10.5006/3833	journal	May 2021
A Review of the Governing Factors in Pit-to-Crack Transitions of Metallic Structures Katona, R. M.; Karasz, E. K.; Schaller, R. F. Corrosion, Vol. 79, Issue 1 https://doi.org/10.5006/4179	journal	November 2022

Similar Records

TOWARDS UNDERSTANDING STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS

Conference · Thu Jun 01 00:00:00 EDT 2023 · OSTI ID:2431306

TOWARDS UNDERSTANDING STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS

Conference · Thu Jun 01 00:00:00 EDT 2023 · OSTI ID:2431307

Towards understanding stress corrosion cracking of austenitic stainless steels exposed to realistic sea salt brines

Citation Formats

References (78)

Similar Records

Related Subjects