A Comparative Analysis on Microstructure and Fracture Mechanism of X100 Pipeline Steel CGHAZ Between Laser Welding and Arc Welding
- The State Key Laboratory of Rolling and Automation of Northeastern University (China)
- Soochow University, School of Iron and Steel (China)
- Jiangsu University of Science and Technology, School of Materials Science and Engineering (China)
The objective of this study is to compare and contrast the differences in microstructure and fracture mechanism between CGHAZ of laser welding and submerged arc welding in X100 pipeline steel. The single-pass welding thermal simulation test of laser welding and submerged arc welding was carried out in MMS-200 thermal simulation test machine using self-made fixtures. The results indicated that the microstructure of laser welding CGHAZ and submerged arc welding CGHAZ was lath martensite and granular bainite, respectively. The impact energy of laser welding CGHAZ was 27 J, and the fracture mode was ductile fracture; the impact energy of submerged arc welding CGHAZ was 7.7 J, and the fracture mode was brittle fracture. The nucleation and propagation mechanism of cracks in different welding modes was established. Microcracks nucleated at the position of dislocation accumulation and remained austenite suppressed crack nucleation in laser welding CGHAZ. The nucleation site was at the M–A constituents in submerged arc welding CGHAZ. The main crack of laser welding CGHAZ was formed by one or a small number of microcracks. The main crack in submerged arc welding CGHAZ was formed by a large number of microcracks. The difference between crack nucleation and propagation mechanism is the reason why the impact energy of laser welding CGHAZ is higher than of submerged arc welding CGHAZ.
- OSTI ID:
- 22970345
- Journal Information:
- Journal of Materials Engineering and Performance, Vol. 28, Issue 11; Other Information: Copyright (c) 2019 ASM International; Country of input: International Atomic Energy Agency (IAEA); ISSN 1059-9495
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Heat Input on M-A Constituent and Toughness of Coarse Grain Heat-Affected Zone in an X100 Pipeline Steel
HAZ fracture properties of Ti-microalloyed offshore steel in as-welded and simulated condition