Magnetic Properties of Ru-Doped Nd{sub 0.67}Sr{sub 0.33}Mn{sub 1−x}Ru{sub x}O{sub 3} (0 ≤ x ≤ 0.10) Manganites
- Barkatullah University, Solid State Physics Laboratory, Department of Physics (India)
- Indian Institute of Science Education and Research (IISER), Department of Physics (India)
The structural and magnetic properties of polycrystalline Nd{sub 0.67}Sr{sub 0.33}Mn{sub 1−x}Ru{sub x}O{sub 3} (x = 0.00 and 0.10) samples have been studied with the substitution of Ru at Mn site. The samples have orthorhombic crystal structure determined by room-temperature X-ray diffraction and Rietvield analysis. On Ru doping at Mn site, a change in its symmetry space group is observed. The increase in Ru content significantly affects the Curie temperature (T{sub c}). The double-exchange mechanism is suppressed with Ru doping affecting the Mn{sup 3+}–O{sup 2−}–Mn{sup 4+} ion network. Paramagnetic regime of samples in magnetization-temperature graph is fitted and analyzed with Curie-Weiss law. The magnetization versus applied magnetic field measurements show that the samples exhibit ferromagnetic behavior at lower temperatures and paramagnetic behavior at room temperature with negligible hysteresis loop and low coercive field.
- OSTI ID:
- 22921206
- Journal Information:
- Journal of Superconductivity and Novel Magnetism, Journal Name: Journal of Superconductivity and Novel Magnetism Journal Issue: 7 Vol. 32; ISSN 1557-1939
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetic, transport and magnetoresistance behavior of Ni doped La{sub 0.67}Sr{sub 0.33}Mn{sub 1−x}Ni{sub x}O{sub 3} (0.00≤x≤0.09) system
The Mean-Field Theory for the Study of the Magnetocaloric Effect of Nd{sub 0.67}Ba{sub 0.33}Mn{sub 0.98}Fe{sub 0.02}O{sub 3} Manganite