Study on Corrosion Behavior of 7075 Aluminum Alloy with Retrogression and Reaging Using Taguchi Method

Journal Article · Thu Nov 15 04:00:00 EST 2018 · Journal of Materials Engineering and Performance

DOI:https://doi.org/10.1007/S11665-018-3677-Z· OSTI ID:22863192

Li, Rongde; Liu, Tong; Su, Ruiming; Su, Jianhao; Qu, Yingdong ^[1]

---

1. Shenyang University of Technology, School of Materials Science and Engineering (China)

The corrosion resistance and mechanical properties of 7075 aluminum alloy are improved by retrogression and reaging (RRA) heat treatment. Due to the complex process of RRA heat treatment, a Taguchi L25 orthogonal array is designed to optimize the process parameters of RRA heat treatment. In this work, analysis of variance was performed to find out the significant heat treatment parameters. Microstructure, mechanical properties, intergranular corrosion, exfoliation corrosion and stress corrosion cracking behaviors of 7075 aluminum alloy after RRA heat treatment were investigated by tensile test, slow strain rate test, transmission electron microscope and scanning electron microscope. Results showed that the RRA treatment involving preaging at 120 °C for 16 h, retrogression at 200 °C for 8 min and reaging at 120 °C for 24 h resulted in a desired combination of corrosion resistance and mechanical properties.

• OSTI ID: 22863192
• Journal Information: Journal of Materials Engineering and Performance, Journal Name: Journal of Materials Engineering and Performance Journal Issue: 11 Vol. 27; ISSN 1059-9495; ISSN JMEPEG
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ALUMINIUM ALLOYS
CORROSION RESISTANCE
CRACKING
HEAT TREATMENTS
INTERGRANULAR CORROSION
MECHANICAL PROPERTIES
MICROSTRUCTURE
SCANNING ELECTRON MICROSCOPY
STRAIN RATE
STRESS CORROSION
TRANSMISSION ELECTRON MICROSCOPY