Effect of Mo-rich Fillers in Pulsed Current Gas Tungsten Arc Welding of Inconel 718 for Improved Strength and Hot Corrosion Resistance

Journal Article · Wed Nov 15 04:00:00 EST 2017 · Journal of Materials Engineering and Performance

DOI:https://doi.org/10.1007/S11665-017-3009-8· OSTI ID:22860773

Bhalodi, Aman Jayesh; Ashokbhai, Harsh Jivani; Balaji, Abhijit; Aravind, S.; Aravind, K. M.; Varma, Vinayak ^[1]

---

1. VIT University, School of Mechanical Engineering (India)

The formation of Laves phase in the fusion zone of Inconel 718 welds is considered to be detrimental and requires major attention, as this phase deteriorates the mechanical properties and high-temperature corrosion resistance. This present study addresses the use of current pulsing technique on the gas tungsten arc welding of 5-mm-thick Inconel 718 plates. Nb-free fillers, namely ERNiCrMo-10 and ERNiCrMo-14, are chosen for joining these plates. Microstructure studies revealed the segregation of Mo-rich phases at the inter-dendritic regions of the fusion zone of both the weldments. Further, the occurrence of detrimental Laves phase was minimized while employing Mo-rich fillers. It is inferred from the tensile studies that the fractures occurred in the parent metal for ERNiCrMo-10 filler and at the fusion zone while employing ERNiCrMo-14. Room-temperature Charpy impact studies also affirm that the impact toughness of ERNiCrMo-10 welds is significantly greater than that of ERNiCrMo-14. Hot corrosion studies were performed on the coupons by exposing them to a synthetic molten salt environment comprising Na{sub 2}SO{sub 4} + 60%V{sub 2}O{sub 5} at 800 °C for 50 h. Owing to the presence of higher amounts of Cr{sub 2}O{sub 3} and NiO, both fusion zones exhibited better hot corrosion resistance than the parent metal. The novel outcome of the study reiterates that with the use of current pulsing and Mo-rich fillers, the detrimental phase shall be controlled.

• OSTI ID: 22860773
• Journal Information: Journal of Materials Engineering and Performance, Journal Name: Journal of Materials Engineering and Performance Journal Issue: 11 Vol. 26; ISSN 1059-9495; ISSN JMEPEG
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
CHROMATES
CHROMIUM OXIDES
CORROSION
CORROSION RESISTANCE
FILLERS
GAS TUNGSTEN-ARC WELDING
INCONEL 718
LAVES PHASES
MICROSTRUCTURE
MOLTEN SALTS
MOLYBDENUM COMPOUNDS
NICKEL OXIDES
PULSE TECHNIQUES
SEGREGATION
TENSILE PROPERTIES
VANADATES
VANADIUM OXIDES
WELDED JOINTS