Nano-Deformation Behavior of a Thermally Aged Duplex Stainless Steel Investigated by Nanoindentation, FIB and TEM
Journal Article
·
· Journal of Materials Engineering and Performance
- University of Science and Technology Beijing, State Key Laboratory for Advanced Metals and Materials (China)
- University of Science and Technology Beijing, Collaborative Innovation Center of Steel Technology (China)
Nanoindentation and electron backscattering diffraction were conducted on a thermally aged duplex stainless steel to investigate the effect of crystal orientation on the plastic deformation behavior during indentation testing. Both nanohardness H and indentation modulus E are correlated with the orientation factor averaged over three normal directions of the contact surface. After thermal aging, the orientation dependence of the hardness and indentation modulus in ferrite significantly changed. For both the ferrite and austenite phases, the maximum and minimum values of the hardness and indentation modulus are given by the near-〈111〉 and near-〈001〉-oriented grains, respectively. The TEM analysis results indicate that the area of plastic deformation in the ferrite grain decreases after thermal aging. The interactions between precipitates and dislocations are considered to be responsible for the degradation of plastic deformation ability in ferrite. The anisotropy of hardness is related to the crystallographic nature and shearing mechanisms.
- OSTI ID:
- 22860296
- Journal Information:
- Journal of Materials Engineering and Performance, Journal Name: Journal of Materials Engineering and Performance Journal Issue: 9 Vol. 27; ISSN 1059-9495; ISSN JMEPEG
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characterization of phase properties and deformation in ferritic-austenitic duplex stainless steels by nanoindentation and finite element method
The effect of grain orientation on nanoindentation behavior of model austenitic alloy Fe-20Cr-25Ni
Effect of deformation bands on phase transformations in a duplex stainless steel
Journal Article
·
Wed Nov 02 20:00:00 EDT 2016
· Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing
·
OSTI ID:1360713
The effect of grain orientation on nanoindentation behavior of model austenitic alloy Fe-20Cr-25Ni
Journal Article
·
Tue Jul 25 20:00:00 EDT 2017
· Acta Materialia
·
OSTI ID:1376458
Effect of deformation bands on phase transformations in a duplex stainless steel
Conference
·
· TMS (The Metallurgical Society) Paper Selection; (USA)
·
OSTI ID:5310365