Effect of a High Magnetic Field on γ′ Phase for Ni-Based Single Crystal Superalloy During Directional Solidification
Journal Article
·
· Metallurgical and Materials Transactions B, Process Metallurgy and Materials Processing Science
- Shanghai University, State Key Laboratory of Advanced Special Steel & Shanghai Key Laboratory of Advanced Ferrometallurgy & School of Materials Science and Engineering (China)
The effect of a high magnetic field on the γ′ phase of Ni-based single crystal superalloy during directional solidification is investigated experimentally. The results clearly indicate that the magnetic field significantly reduces the γ′ phase size. Further, the quenching experiment is carried out, and the results found that the length of mushy zone is obviously decreased under a high magnetic field. Based on both experimental results and nucleation mechanism, it is found that the decrease of γ′ phase size should be attributed to the fact that a high magnetic field causes the increase of temperature gradient in front of solid/liquid interface and leads to the increase of undercooling of γ′ phase.
- OSTI ID:
- 22857882
- Journal Information:
- Metallurgical and Materials Transactions B, Process Metallurgy and Materials Processing Science, Vol. 49, Issue 4; Other Information: Copyright (c) 2018 The Minerals, Metals & Materials Society and ASM International; http://www.springer-ny.com; Country of input: International Atomic Energy Agency (IAEA); ISSN 1073-5615
- Country of Publication:
- United States
- Language:
- English
Similar Records
A comparative study of quantitative microsegregation analyses performed during the solidification of the Ni-base superalloy CMSX-10
Influence of temperature on the lattice misfit and elastic moduli of a Ni based single crystal superalloy with high volume fraction of γ′ phase
Influence of Melt Superheating Treatment on Solidification Characteristics and Rupture Life of a Third-Generation Ni-Based Single-Crystal Superalloy
Journal Article
·
Sat Mar 01 00:00:00 EST 2014
· Materials Characterization
·
OSTI ID:22857882
+3 more
Influence of temperature on the lattice misfit and elastic moduli of a Ni based single crystal superalloy with high volume fraction of γ′ phase
Journal Article
·
Wed Aug 15 00:00:00 EDT 2018
· Materials Characterization
·
OSTI ID:22857882
+3 more
Influence of Melt Superheating Treatment on Solidification Characteristics and Rupture Life of a Third-Generation Ni-Based Single-Crystal Superalloy
Journal Article
·
Wed Aug 15 00:00:00 EDT 2018
· Metallurgical and Materials Transactions B, Process Metallurgy and Materials Processing Science
·
OSTI ID:22857882
+3 more