Formation Mechanism of Nanoscale Al{sub 3}Fe Phase in Al-Fe Alloy During Semisolid Forming Process

Journal Article · Mon Oct 15 04:00:00 EDT 2018 · Metallurgical and Materials Transactions B, Process Metallurgy and Materials Processing Science

DOI:https://doi.org/10.1007/S11663-018-1323-7· OSTI ID:22857851

Wang, Xiang; Guan, Ren-Guo; Wang, Yu ^[1]

---

1. Northeastern University, School of Materials Science and Engineering (China)

The formation mechanism of nanoscale Al{sub 3}Fe phase in Al-1Fe (wt pct) alloy during rheo-extrusion was investigated, and the mechanical property of the prepared alloy was also measured. The results show that the average length of Al{sub 3}Fe phase in Al-1Fe alloy prepared by rheo-extrusion is 300 nm, which is much more refined than the needlelike Al{sub 3}Fe phase in as-cast Al-1Fe alloy (50 μm). In rheo-extrusion, Al{sub 3}Fe phase formed by eutectic reaction is bonelike, but it could be continuously refined by the shear deformation in the wheel groove, in equal channel angular flow, and in expansion extrusion mold. The total equivalent strain of the shear deformation is higher than 4.82. The tensile strength and elongation of Al-1Fe alloy prepared by rheo-extrusion are 135 MPa and 30 pct, respectively. The tensile strength of Al-1Fe alloy prepared by rheo-extrusion is 58.8 pct higher than that of as-cast Al-1Fe alloy, and the elongation is 19 pct higher than that of as-cast Al-1Fe alloy. Compared with as-cast Al-1Fe alloy, the improvements of tensile strength and elongation caused by shear deformation in rheo-extrusion are higher than the reported improvements induced by rare earth modification.

• OSTI ID: 22857851
• Journal Information: Metallurgical and Materials Transactions B, Process Metallurgy and Materials Processing Science, Journal Name: Metallurgical and Materials Transactions B, Process Metallurgy and Materials Processing Science Journal Issue: 5 Vol. 49; ISSN 1073-5615; ISSN MTBSEO
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ALUMINIUM ALLOYS
CASTING MOLDS
ELONGATION
EUTECTICS
EXPANSION
EXTRACTION
EXTRUSION
IRON ALLOYS
NANOSTRUCTURES
PRESSURE RANGE MEGA PA
RARE EARTHS
SHEAR
STRAINS
TENSILE PROPERTIES