In-situ microstructural observation of Ti-Cu alloys for semi-solid processing
- University of Campinas, School of Mechanical Engineering, Campinas, SP (Brazil)
- University of Wollongong, School of Mechanical, Materials, Mechatronic and Biomedical Engineering, Wollongong, NSW (Australia)
The semi-solid processing of metallic alloys strongly depends on the microstructural features exhibited by the raw material. Consequently, many characterization techniques have been used to elucidate semi-solid microstructures. In the present work, high-temperature laser-scanning confocal microscopy (HT-LSCM) was used to characterize Ti-Cu alloys intended for thixoforming. During the reheating stage, this in-situ technique enabled us to observe the Ti-β grains formed through the reverse eutectoid transformation. Furthermore, the results showed that thermomechanical treatment was primarily responsible for breaking up the dendritic microstructure. The liquid formation and peritectic temperature were easily determined via the HT-LSCM investigation. Prior to the reverse peritectic reaction, which corresponds to the onset of equilibrium melting, we obtained experimental evidence of the melting of non-equilibrium phases that originated via segregation during solidification. Finally, it was possible to qualitatively study the coarsening mechanisms that occurred in the semi-solid state. Irrespective of the alloy composition (liquid fraction), both Ostwald ripening and coalescence occurred during the isothermal heat treatments. Based on the obtained results, HT-LCSM can be considered a valuable technique for the characterization of thixotropic alloys.
- OSTI ID:
- 22805830
- Journal Information:
- Materials Characterization, Vol. 145; Other Information: Copyright (c) 2017 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ostwald ripening of faceted Si particles in an Al-Si-Cu melt
Effect of Ultrasonic Treatment on the Microstructure of A201 Aluminium Alloy for Thixoforming