Environmentally Friendly Chitosan-g-poly(acrylic acid-co-acrylamide)/Ground Basalt Superabsorbent Composite for Agricultural Applications
- Higher Institute for Applied Sciences and Technology, Laboratory of Materials Sciences, Department of Applied Physics (Syrian Arab Republic)
This paper investigates on the preparation of a novel eco-friendly composite hydrogel, chitosan-g-poly(acrylic acid-co-acrylamide)/ground basalt and its potential application as a soil ameliorant. Synthesis was undergone using microwave irradiation. N,N′-methylene bisacrylamide MBA was used as a cross-linker, whereas potassium peroxydisulfate KPS and N,N,N′,N′-tetramethylene diamine TEMED were used as radical initiator and reaction accelerator, respectively. The incorporation of ground basaltic rocks into the hydrogel was very beneficial: (i) It lowers the cost of the final hydrogel, (ii) It enhances the mechanical strength of the hydrogel, (iii) It boosts the maximum water absorbency of the composite, 650 g/g versus 450 g/g for the hydrogel without basalt and (iv) It promotes the thermal stability of the composite in comparison with the hydrogel alone. The prepared composite hydrogel was characterized by FTIR, X-ray diffractometer and scanning electron microscope SEM. The effects of pH and ionic strength on water absorbency were also investigated. The role of the prepared composite as a soil conditioner is performed using eggplant (Solanum melongena) as a model.
- OSTI ID:
- 22787968
- Journal Information:
- Journal of Polymers and the Environment, Journal Name: Journal of Polymers and the Environment Journal Issue: 9 Vol. 26; ISSN 1566-2543
- Country of Publication:
- United States
- Language:
- English
Similar Records
Environmentally Responsive Poly(N-isopropylacrylamide)-co-poly(acrylic acid) Hydrogels for Separation of Toxic Metals and Organic Explosive Compounds from Water
Poly(N,N-dimethylacrylamide-co-acrylamide) Grafted Hydroxyethyl Cellulose Hydrogel: A Useful Congo Red Dye Remover