Study on Microwave Performance of Low-Temperature Sintered, Ba(CoTi){sub 1.5}Fe{sub 9}O{sub 19} Ferrite for Application at UHF Frequency
- University of Electronic Science and Technology of China, State Key Laboratory of Electronic Thin Films and Integrated Devices (China)
M-type barium ferrite, Ba(CoTi){sub 1.5}Fe{sub 9}O{sub 19}, was synthesized via the solid-state reaction method. BBSZ, i.e., B{sub 2}O{sub 3} −Bi{sub 2}O{sub 3} −SiO{sub 2} −ZnO, was added to adjust the sintering temperature to values lower than that of silver (i.e., ∼961 °C). The phase formation characteristics, microstructure, magnetic, and microwave properties were characterized by x-ray diffraction, scanning electron microscope, vibrating sample magnetometer, and impedance analyzer, respectively. The results show that densification of samples were enhanced by increasing the amount of BBSZ with corresponding gains realized in magnetic properties. Such enhanced properties in Ba(CoTi){sub 1.5}Fe{sub 9}O{sub 19} are attributed to the low-melting point experienced as the result of BBSZ glass additives which gave rise to the stabilization of a liquid phase during sintering.
- OSTI ID:
- 22774134
- Journal Information:
- Journal of Superconductivity and Novel Magnetism, Vol. 31, Issue 2; Other Information: Copyright (c) 2018 Springer Science+Business Media, LLC, part of Springer Nature; Article Copyright (c) 2017 Springer Science+Business Media New York; http://www.springer-ny.com; Country of input: International Atomic Energy Agency (IAEA); ISSN 1557-1939
- Country of Publication:
- United States
- Language:
- English
Similar Records
High frequency permeability and permittivity spectra of BiFeO{sub 3}/(CoTi)-BaM ferrite composites
Microstructure and Magnetic Properties of Ba{sub 0.95}Y{sub 0.05}Fe{sub 12−x}Co{sub x}O{sub 19} Hexaferrites
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BARIUM COMPOUNDS
BISMUTH OXIDES
BORON OXIDES
FERRITES
LIQUIDS
MAGNETIC PROPERTIES
MELTING POINTS
MICROSTRUCTURE
MICROWAVE RADIATION
SCANNING ELECTRON MICROSCOPY
SILICON OXIDES
SILVER
SINTERING
SOLIDS
VIBRATING SAMPLE MAGNETOMETERS
X-RAY DIFFRACTION
ZINC OXIDES