A quasi-in-situ EBSD observation of the transformation from rolling texture to recrystallization texture in V-4Cr-4Ti alloy

Journal Article · Sat Apr 15 04:00:00 EDT 2017 · Materials Characterization

DOI:https://doi.org/10.1016/J.MATCHAR.2017.01.037· OSTI ID:22689734

Peng, Lixia ^[1]; Li, Xiongwei ^[2]; Fan, Zhijian ^[3]; Jiang, Chunli; Zhou, Ping ^[1]; Lai, Xinchun ^[1]

---

1. Institute of Materials Research, China Academy of Engineering Physics, Jiangyou, Sichuan Province 621908 (China)
2. Institute of Metal Research, China Academy of Sciences, 72 Wenhua Road, Shenyang 110016 (China)
3. Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang, Sichuan Province 621900 (China)

Recrystallization texture evolution of rolled V-4Cr-4Ti alloy has been investigated by quasi-in-situ EBSD (electron back-scattering diffraction) method. Concurrently, the precipitates were characterized by SEM (Scanning Electron Microscopy). It was found that both the initial rolling textures and the distribution of the precipitates affected the formation of the recrystallization texture. It was revealed that the texture transformations of (558) 〈110〉 + (665) 〈110〉 to (334) 〈483〉 + (665) 〈1 1 2.4〉 were possibly attributed to the selective drag induced by the sparsely dispersed Ti-rich precipitates. While the densely distributed Ti-rich precipitates were responsible for the randomized recrystallization texture. Finally, when the precipitates were absent, the orientation changes from (112) 〈110〉 and (558) 〈110〉 to (111) 〈112〉 and (001) <110> to (001) <520> were observed. - Highlights: • Micro recrystallization texture evolution in V-4Cr-4Ti alloys is reported for the first time. • The volume fraction of Ti-rich precipitates has significant effect on the recrystallization texture evolution. • The dissolution of the Ti-rich precipitates above 1100 °C induces the strengthening of (111) <112> texture.

• OSTI ID: 22689734
• Journal Information: Materials Characterization, Journal Name: Materials Characterization Vol. 126; ISSN 1044-5803; ISSN MACHEX
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
BACKSCATTERING
CHROMIUM ALLOYS
DIFFRACTION METHODS
DISSOLUTION
DISTRIBUTION
DRAG
ELECTRON DIFFRACTION
PRECIPITATION
RECRYSTALLIZATION
ROLLING
SCANNING ELECTRON MICROSCOPY
TEXTURE
TITANIUM ALLOYS
VANADIUM ALLOYS