A fresnoite-structure-related mixed valent titanium(III/IV) chlorosilicate, Ba{sub 3}Ti{sub 2}Si{sub 4}O{sub 14}Cl: A flux crystal growth route to Ti(III) containing oxides
Single crystals of mixed valent barium titanium(III/IV) chlorosilicate, Ba{sub 3}Ti{sub 2}Si{sub 4}O{sub 14}Cl{sub 0.91}O{sub 0.09}, were grown in a high temperature molten chloride flux involving an in situ reduction step. The fresnoite structure related Ba{sub 3}Ti{sub 2}Si{sub 4}O{sub 14}Cl{sub 0.91}O{sub 0.09} crystallizes in the tetragonal space group P4/mbm with lattice parameters of a=8.6717(2) Å, c=18.6492(5) Å. The title compound exhibits a 3D structure consisting of 2D layers of fused Ti{sub 2}O{sub 9} and Si{sub 4}O{sub 12} groups and 2D layers of fused Ti{sub 2}O{sub 9}Cl{sub 2} and Si{sub 2}O{sub 7} groups that are linked via barium atoms. The in situ reduction of Ti(IV) to Ti(III) is achieved via the addition of metallic Mg to the flux to function as the reducing agent. The temperature dependence of the magnetic susceptibility shows simple paramagnetism above 100 K. There is a discontinuity in the susceptibility data below 100 K, which might be due to a structural change that takes place resulting in charge ordering. - Graphical abstract: The fresnoite structure related novel reduced barium titanium chlorosilicate, Ba{sub 3}Ti{sub 2}Si{sub 4}O{sub 14}Cl{sub 0.91}O{sub 0.09}, were synthesized via flux method. An in situ reduction of Ti(IV) to Ti(III) achieved using Mg metal. The 3D structure consists 2D layers of fused Ti{sub 2}O{sub 9} and Si{sub 4}O{sub 12} and 2D layers of fused Ti{sub 2}O{sub 9}Cl{sub 2} and Si{sub 2}O{sub 7} connected via barium atoms. Compound shows simple paramagnetism above 100 K. - Highlights: • The fresnoite related Ba{sub 3}Ti{sub 2}Si{sub 4}O{sub 14}Cl{sub 0.91}O{sub 0.09} were grown via molten flux method. • The in situ reduction of Ti(IV) to Ti(III) is achieved using metallic Mg. • 2D layers of Ti{sub 2}O{sub 9} and Si{sub 4}O{sub 12} and Ti{sub 2}O{sub 9}Cl{sub 2} and Si{sub 2}O{sub 7} connect via Ba atoms. • The magnetic susceptibility shows simple paramagnetism above 100 K.
- OSTI ID:
- 22658296
- Journal Information:
- Journal of Solid State Chemistry, Vol. 250; Other Information: Copyright (c) 2017 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crystal structures of strontium and barium ethylenediaminetetraacetato cobaltates(III), Sr[CoEdta]{sub 2}.9H{sub 2}O and Ba[CoEdta]{sub 2}.8H{sub 2}O: Comparison of the structures of complexes in the series M'[CoEdta]{sub 2}.nH{sub 2}O (M' = Mg, Ca, Sr, Ba; n = 7-10)
Structural insights into the thermal decomposition sequence of barium tetrahydrogenorthotellurate(VI), Ba[H{sub 4}TeO{sub 6}]
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
BARIUM
BARIUM COMPOUNDS
CRYSTAL GROWTH
EXPERIMENTAL DATA
LATTICE PARAMETERS
LAYERS
MAGNETIC SUSCEPTIBILITY
OXIDES
PARAMAGNETISM
REDUCING AGENTS
REDUCTION
SPACE GROUPS
TEMPERATURE DEPENDENCE
TEMPERATURE RANGE 0065-0273 K
TEMPERATURE RANGE 0400-1000 K
TITANIUM IONS