Large structural modulations in the relaxor ferroelectric and intermediate state of strontium rich members (x>0.6) of the Sr{sub x}Ba{sub 1−x}Nb{sub 2}O{sub 6} (sbn) solid solution series
The amplitudes of the positional, occupational and adp modulations of sbn mixed crystals are strongly enhanced for high strontium contents. The increase of structural modulations is accompanied by reduced spontaneous electric polarization largely due to smaller off-center shifts of the niobium atoms. Beyond the room temperature ferroelectric – intermediate transition near x=0.77, anomal large U{sub 33} atomic displacement parameters of the niobium atoms indicate static disorder caused by loss of orientational coupling between residual shifts of Nb atoms in neighboring NbO{sub 6} octahedra. Change of satellite intensities show a reduction from two-dimensional to one-dimensional modulation which is not consistent with tetragonal symmetry. The pseudo-tetragonally twinned crystal structure of sbn82 was refined in the orthorhombic super-space group A2mm(½0γ)000. The apparent tetragonal symmetry of the other investigated sbn samples also seems to be due to pseudo tetragonal twinning with equal twin volumes. The modulations mainly consist of cooperatively tilted NbO{sub 6} octahedra and wave-like ordered incomplete occupation of the largest cation sites (Me2a and b) by Ba{sup 2+} and Sr{sup 2+}. Furthermore, the atomic displacement parameters of the Me2 sites are strongly modulated. - Graphical abstract: Satellite reflections and modulation coefficients in the solid solution series Sr{sub x}Ba{sub 1−x}Nb{sub 2}O{sub 6}. - Highlights: • The modulationed structures are refined for the whole composition range of sbn32–sbn82 in tetragonal and orthorhombic setting. • The amplitudes of positional, occupational and adp modulations increase strongly with the strontium content. • Evidence is presented that the sbn crystals are pseudo tetragonally twinned. • The ferroelectric–intermediate paraelectric transition is not accompanied by a change of symmetry. • Anomal adp of intermediate (non-ferroelectric) sbn82 indicate loss of coupling between off-center shifts of neighboring niobium.
- OSTI ID:
- 22658180
- Journal Information:
- Journal of Solid State Chemistry, Vol. 246; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Site occupancy and cation binding states in reduced polycrystalline Sr{sub x}Ba{sub 1−x}Nb{sub 2}O{sub 6}
Structural characterization and Curie temperature determination of a sodium strontium niobate ferroelectric nanostructured powder
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
37 INORGANIC
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ADP
ATOMIC DISPLACEMENTS
BARIUM COMPOUNDS
BARIUM IONS
CRYSTALS
FERROELECTRIC MATERIALS
INTERMEDIATE STATE
NIOBIUM
NIOBIUM OXIDES
ORTHORHOMBIC LATTICES
SOLID SOLUTIONS
SPACE GROUPS
STRONTIUM COMPOUNDS
STRONTIUM IONS