Synthesis, crystal structure, and ionic conductivity of a new layered metal phosphate, Li{sub 2}Sr{sub 2}Al(PO{sub 4}){sub 3}
- Department of Energy Systems Research, Ajou University, Suwon 16499 (Korea, Republic of)
- Advanced Materials & Devices Laboratory, Korea Institute of Energy Research, Daejeon 34129 (Korea, Republic of)
A new layered metal phosphate, Li{sub 2}Sr{sub 2}Al(PO{sub 4}){sub 3}, was synthesized in the form of either a single-crystal or polycrystalline powder using the molten hydroxide flux method or a solid-state reaction, respectively. Li{sub 2}Sr{sub 2}Al(PO{sub 4}){sub 3} crystallizes to the P2{sub 1}/n (Z=4) monoclinic space group with lattice parameters a≈4.95 Å, b≈22.06 Å, c≈8.63 Å, and β≈91.5°. The structure is composed of stacked [LiSrAl(PO{sub 4}){sub 2}] layers alternating regularly with [LiSrPO{sub 4}] layers. In the [LiSrAl(PO{sub 4}){sub 2}] sublattice, the AlO{sub 6} octahedra and PO{sub 4} tetrahedra are tilted cooperatively to form an anionic, corrugated, two-dimensional [Al(PO{sub 4}){sub 2}]{sup 3−} framework that can be regarded as a “distorted-glaserite” structure. The [LiSrPO{sub 4}] sublattice is that of a layered block containing a six-membered ring formed from alternating linkages of LiO{sub 4} and PO{sub 4} tetrahedra. The six-membered rings show a boat-type arrangement with the up(U) or down(D) pointing sequence, UUDUUD. The interspace between the two sublattices generates a two-dimensional pathway for Li{sup +} ion conduction. The impedance measurement indicated that Li{sub 2}Sr{sub 2}Al(PO{sub 4}){sub 3} had a moderate ion conductivity (σ≈1.30×10{sup −4} S cm{sup −1} at 667 K), with an activation energy E{sub a}≈1.02 eV. - Graphical abstract: Polyhedral view of Li{sub 2}Sr{sub 2}Al(PO{sub 4}){sub 3}. Li{sup +} ions are represented by green spheres, Sr atoms by white spheres, AlO{sub 6} groups by octahedra, and PO{sub 4} groups by tetrahedra. - Highlights: • New compound Li{sub 2}Sr{sub 2}Al(PO{sub 4}){sub 3} is reported. • The crystal structure is investigated by single-crystal XRD analysis. • The structure is formed by the alternate stacking of two different sublattices. • Correlation between the crystal structure and ionic conductivity is discussed.
- OSTI ID:
- 22658076
- Journal Information:
- Journal of Solid State Chemistry, Vol. 243; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crystal structure and ion conductivity of a new mixed-anion phosphate LiMg{sub 3}(PO{sub 4})P{sub 2}O{sub 7}
Crystal structures and electronic properties for the over-lithiated and Li–Ag substituted phases of Li{sub 9}V{sub 3}(P{sub 2}O{sub 7}){sub 3}(PO{sub 4}){sub 2} insertion electrode system