Er{sub 1.33}Pt{sub 3}Ga{sub 8}: A modulated variant of the Er{sub 4}Pt{sub 9}Al{sub 24}-structure type

Journal Article · Sat Oct 15 00:00:00 EDT 2016 · Journal of Solid State Chemistry

DOI:https://doi.org/10.1016/J.JSSC.2016.04.009· OSTI ID:22658068

Oswald, Iain W.H. ^[1]; Gourdon, Olivier ^[2]; Bekins, Amy; Evans, Jess ^[3]; Treadwell, LaRico J. ^[1]

---

1. Department of Chemistry and Biochemistry, University of Texas at Dallas, Richardson, TX 75080 (United States)
2. Research and Development, ZS Pharma, Coppell, TX 75109 (United States)
3. Department of Chemistry and Biochemistry, University of Texas at Arlington, Arlington, TX 76019 (United States)

Single crystals of Er{sub 1.33}Pt{sub 3}Ga{sub 8} were synthesized in a molten Ga flux. Er{sub 1.33}Pt{sub 3}Ga{sub 8} can be considered to be a modulated variant of the Er{sub 4}Pt{sub 9}Al{sub 24}-structure type, where the partial occupancies are ordered. Indeed, the presence of weak satellite reflections indicates a complex organization and distribution of the Er and Ga atoms within the [ErGa] slabs. The structure has been solved based on single crystal X-ray diffraction data in the monoclinic superspace group X2/m(0β0)00 with a commensurate modulated vector q=1/3b*. Precession images also indicate diffusion in the perpendicular direction indicating a partial disorder of this arrangement from layer to layer. In addition, Er{sub 1.33}Pt{sub 3}Ga{sub 8} shows antiferromagnetic ordering at T{sub N}~5 K. - Graphical abstract: A precession image of the hk0 zone showing weak, periodic, unindexed reflections indicating modulation and representation of the commensurate [ErGa] layer showing the waving modulated occupation. - Highlights: • Single crystals of Er{sub 1.33}Pt{sub 3}Ga{sub 8} were grown from gallium flux. • The structure of Er{sub 1.33}Pt{sub 3}Ga{sub 8} is compared to Er{sub 4}Pt{sub 9}Al{sub 24}. • Structure has been solved in the monoclinic superspace group X2/m(0β0)00 with a commensurate modulated vector q=1/3b*.

• OSTI ID: 22658068
• Journal Information: Journal of Solid State Chemistry, Vol. 242, Issue Part 2; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
• Country of Publication: United States
• Language: English

Related Subjects

37 INORGANIC
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
36 MATERIALS SCIENCE
ALUMINIUM COMPOUNDS
CRYSTAL GROWTH
ERBIUM COMPOUNDS
LAYERS
MONOCLINIC LATTICES
MONOCRYSTALS
PLATINUM COMPOUNDS
X RADIATION
X-RAY DIFFRACTION