AgI alloying in SnTe boosts the thermoelectric performance via simultaneous valence band convergence and carrier concentration optimization

Journal Article · Sat Oct 15 04:00:00 EDT 2016 · Journal of Solid State Chemistry

DOI:https://doi.org/10.1016/J.JSSC.2016.02.012· OSTI ID:22658055

Banik, Ananya; Biswas, Kanishka

SnTe, a Pb-free analogue of PbTe, was earlier assumed to be a poor thermoelectric material due to excess p-type carrier concentration and large energy separation between light and heavy hole valence bands. Here, we report the enhancement of the thermoelectric performance of p-type SnTe by Ag and I co-doping. AgI (1–6 mol%) alloying in SnTe modulates its electronic structure by increasing the band gap of SnTe, which results in decrease in the energy separation between its light and heavy hole valence bands, thereby giving rise to valence band convergence. Additionally, iodine doping in the Te sublattice of SnTe decreases the excess p-type carrier concentration. Due to significant decrease in hole concentration and reduction of the energy separation between light and heavy hole valence bands, significant enhancement in Seebeck coefficient was achieved at the temperature range of 600–900 K for Sn{sub 1−x}Ag{sub x}Te{sub 1−x}I{sub x} samples. A maximum thermoelectric figure of merit, zT, of ~1.05 was achieved at 860 K in high quality crystalline ingot of p-type Sn{sub 0.95}Ag{sub 0.05}Te{sub 0.95}I{sub 0.05}. - Graphical abstract: Significant decrease in hole concentration and reduction of the energy separation between light and heavy hole valence bands resulted in a maximum thermoelectric figure of merit, zT, of ~1.05 at 860 K in high quality crystalline ingot of p-type Sn{sub 0.95}Ag{sub 0.05}Te{sub 0.95}I{sub 0.05}. - Highlights: • AgI alloying in SnTe increases the principle band gap. • Hole concentration reduction and valence band convergence enhances thermopower of SnTe-AgI. • A maximum zT of ~1.05 was achieved at 860 K in p-type Sn{sub 0.95}Ag{sub 0.05}Te{sub 0.95}I{sub 0.05}.

• OSTI ID: 22658055
• Journal Information: Journal of Solid State Chemistry, Journal Name: Journal of Solid State Chemistry Journal Issue: Part 2 Vol. 242; ISSN 0022-4596; ISSN JSSCBI
• Country of Publication: United States
• Language: English

Related Subjects

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CHEMISTRY
ABUNDANCE
CONCENTRATION RATIO
CONVERGENCE
DOPED MATERIALS
ELECTRONIC STRUCTURE
EXPERIMENTAL DATA
MONOCRYSTALS
PERFORMANCE
SILVER IODIDES
TEMPERATURE RANGE 0400-1000 K
THERMOELECTRIC MATERIALS
TIN TELLURIDES
VALENCE