Synthesis and structure determination of the novel aluminophosphate TL-1: A new layered compound with corner-sharing AlX{sub 6} chains
- Dipartimento di Scienze della Terra, Università di Torino, Via Valperga Caluso 35, I-10125 Torino (Italy)
- Dipartimento di Chimica, Università di Torino, Via Pietro Giuria 7, I-10125 Torino (Italy)
A novel layered aluminophosphate (TL-1) has been synthesized. Crystals grow as pseudo-hexagonal thin platelets and their whole morphology depends on the synthesis conditions. The structure was solved by single-crystal X-ray diffraction using charge flipping methods. The synthesized layered material, with composition [AlPO{sub 4}F(H{sub 2}O)]-(H{sub 10}C{sub 4}ON){sub 4}, crystallizes in the monoclinic space group P2{sub 1}/a with a=9.2282(5) Å, b=6.9152(4) Å, c=14.4615(9) Å, β=101.57(1)°. The novel compound has corner sharing AlO{sub 3}F{sub 2}(H{sub 2}O) octahedral chains running along [010], where fluorine atoms are at the shared apices, three oxygen atoms are shared with PO{sub 4} tetrahedra while the sixth oxygen pertain to an H{sub 2}O molecule. The stability field of the novel material is enclosed in the HF/Al{sub 2}O{sub 3} ratio ranging between 1 and 4 and the HF/morpholine ratio lower than 3. At temperature lower than 190 °C, the synthesis results is a pure aluminophosphate sample (low alumina/morpholine ratio). A treatment with H{sub 2}CO{sub 3} leads to a complete morpholine removal, as shown by in situ Raman spectroscopy. Powder X-ray diffraction reveals that, after morpholine extraction, the material collapses. The collapse is irreversible. - Highlights: • A new layered aluminophosphate was obtained and characterized. • The crystal structure is a sequence of aluminophosphate and organic layers. • The stability field of the new phase was defined by changing chemistry and T. • The templating agent can be removed by using a CO{sub 2} aqueous solution. • The decomposition of the morpholine induce a collapse in the structure.
- OSTI ID:
- 22658026
- Journal Information:
- Journal of Solid State Chemistry, Vol. 242, Issue Part 1; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
A NEW CLASS MESOPOROUS ALUMINOPHOSPHATES AS POTENTIAL CATALYSTS IN THE UPGRADING PETROLEUM FEEDSTOCKS
The synthesis and structure of a chiral 1D aluminophosphate chain compound: d-Co(en){sub 3}[AlP{sub 2}O{sub 8}].6.5H{sub 2}O