Magnetic properties and coercivity mechanism of Sm{sub 1-x}Pr{sub x}Co{sub 5} (x=0-0.6) nanoflakes prepared by surfactant-assisted ball milling

Journal Article · Sun May 15 04:00:00 EDT 2016 · AIP Advances

DOI:https://doi.org/10.1063/1.4944401· OSTI ID:22611751

Xu, M. L.; Wu, Q.; Li, Y. Q.; Lu, Q. M. ^[1]

---

1. College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124 (China)

Sm{sub 1-x}Pr{sub x}Co{sub 5} (x=0-0.6) nanoflakes with CaCu{sub 5} structure were successfully prepared by surfactant-assisted high-energy ball milling (SAHEBM). The crystal structure and magnetic properties of Sm{sub 1-x}Pr{sub x}Co{sub 5} (x=0-0.6) nanoflakes were studied by X-ray diffraction and vibrating sample magnetometer. Effects of Pr addition on the structure, magnetic properties and coercivity mechanism of Sm{sub 1-x}Pr{sub x}Co{sub 5} nanoflakes were systematically investigated. XRD results show that all the nanoflakes have a hexagonal CaCu{sub 5}-type (Sm, Pr){sub 1}Co{sub 5} main phase and the (Sm, Pr){sub 2}Co{sub 7} impurity phase, and all of the samples exhibit a strong (00l) texture after magnetic alignment. As the Pr content increases, remanence firstly increases, then slightly reduced, while anisotropy field (H{sub A}) and H{sub ci} of decrease monotonically. Maximum energy product [(BH){sub max}] of the flakes increases first, peaks at 24.4 MGOe with Pr content of x = 0.4, then drops again. Magnetization behavior analysis indicate that the coercivity mechanism is mainly controlled by inhomogeneous domain wall pinning, and the pinning strength weakens with the increased Pr content, suggesting the great influence of H{sub A} on the coercivity of flakes.

• OSTI ID: 22611751
• Journal Information: AIP Advances, Journal Name: AIP Advances Journal Issue: 5 Vol. 6; ISSN AAIDBI; ISSN 2158-3226
• Country of Publication: United States
• Language: English

Related Subjects

75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ALIGNMENT
ANISOTROPY
COBALT COMPOUNDS
COERCIVE FORCE
CRYSTAL STRUCTURE
CRYSTALS
IMPURITIES
MAGNESIUM OXIDES
MAGNETIC FLUX
MAGNETIC PROPERTIES
MAGNETIZATION
MILLING
PRASEODYMIUM COMPOUNDS
SAMARIUM COMPOUNDS
SURFACTANTS
VIBRATING SAMPLE MAGNETOMETERS
X-RAY DIFFRACTION