Dielectric and AC conductivity studies of Nd substituted 0.8BaTiO{sub 3}-0.2(Bi{sub 0.5(1-x)}Nd{sub 0.5x}K{sub 0.5})TiO{sub 3} lead free ceramics
0.8BaTiO{sub 3} – 0.2(Bi{sub 0.5(1-x)}Nd{sub 0.5x}K{sub 0.5})TiO{sub 3} (0.01 ≤ x ≤ 0.06) lead free ceramic materials have been prepared by solid state reaction method and followed by high energy ball milling process. X-ray diffraction studies confirm the tetragonal structure of the materials at room temperature. Lattice parameters and density are decreasing with increase of Nd substitution. Microstructure studies were done by using Scanning electron microscope and it found that grain size is decreasing with increase of Nd substitution. Temperature and frequency dependent dielectric studies reveal relaxor behaviour of the materials. Dielectric constant, dielectric loss and Curie temperature are decreasing with Nd substitution. Maximum Curie temperature of 195°C was observed at 1 MHz for x=0.01 Nd substituted sample. Degree of diffuseness was calculated from the modified Curie-Weiss law and it is increasing with Nd substitution. AC conductivity is increasing with increase of Nd substitution and observed maximum activation energy of 0.52 eV for x=0.02 Nd substituted sample.
- OSTI ID:
- 22608804
- Journal Information:
- AIP Conference Proceedings, Vol. 1731, Issue 1; Conference: DAE solid state physics symposium 2015, Uttar Pradesh (India), 21-25 Dec 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Atomistic simulation and ab initio study of the defect structure of spinel-related Li{sub 0.5−0.5x}Mg{sub x}Fe{sub 2.5−0.5x}O{sub 4}
Effect of Pb(Fe{sub 1/2}Nb{sub 1/2})O{sub 3} modification on dielectric and piezoelectric properties of Pb(Mg{sub 1/3}Nb{sub 2/3})O{sub 3}-PbZr{sub 0.52}Ti{sub 0.48}O{sub 3} ceramics
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ACTIVATION ENERGY
BISMUTH COMPOUNDS
CERAMICS
CURIE POINT
CURIE-WEISS LAW
DIELECTRIC MATERIALS
FREQUENCY DEPENDENCE
GRAIN SIZE
LATTICE PARAMETERS
MILLING
NEODYMIUM ADDITIONS
NEODYMIUM COMPOUNDS
PERMITTIVITY
POTASSIUM COMPOUNDS
SCANNING ELECTRON MICROSCOPY
SOLIDS
TEMPERATURE RANGE 0273-0400 K
TITANATES
TITANIUM OXIDES
X-RAY DIFFRACTION