Grain size effect on activation energy in spinel CoFe{sub 2}O{sub 4} ceramic
Journal Article
·
· AIP Conference Proceedings
- Department of Physics, Indian Institute of Technology Patna, Patna-800013 (India)
Cobalt ferrite of different average crystallites (from nanocrystallite to micro crystallites) has been prepared by the Sol-Gel Method. The X-ray diffraction (XRD) analysis confirms the cubic spinel phase with no trace of impurity phases. The effect of annealing temperature on micro structure and electric transport properties as a function of frequency and temperature has been studied. It is observed that the electric impedance and conductivity are strongly dependent on grain size. The impedance spectroscopic study is employed to understand the electrical transport properties of cobalt ferrite.
- OSTI ID:
- 22608791
- Journal Information:
- AIP Conference Proceedings, Vol. 1731, Issue 1; Conference: DAE solid state physics symposium 2015, Uttar Pradesh (India), 21-25 Dec 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Polyethylene glycol coated CoFe{sub 2}O{sub 4} nanoparticles: A potential spinel ferrite for biomedical applications
Tuning the Magnetic Properties of ZnFe{sub 2}O{sub 4} Nanoparticles Through Partial Doping and Annealing
Comparative study of NiFe{sub 2−x}Al{sub x}O{sub 4} ferrite nanoparticles synthesized by chemical co-precipitation and sol–gel combustion techniques
Journal Article
·
Wed Jun 24 00:00:00 EDT 2015
· AIP Conference Proceedings
·
OSTI ID:22608791
+2 more
Tuning the Magnetic Properties of ZnFe{sub 2}O{sub 4} Nanoparticles Through Partial Doping and Annealing
Journal Article
·
Mon Apr 15 00:00:00 EDT 2019
· Journal of Superconductivity and Novel Magnetism
·
OSTI ID:22608791
Comparative study of NiFe{sub 2−x}Al{sub x}O{sub 4} ferrite nanoparticles synthesized by chemical co-precipitation and sol–gel combustion techniques
Journal Article
·
Fri Jun 15 00:00:00 EDT 2012
· Materials Research Bulletin
·
OSTI ID:22608791