Surface and magnetic characteristics of Ni-Mn-Ga/Si (100) thin film
- Defence Metallurgical Research Laboratory, Hyderabad – 500 058 (India)
- School of Advanced Sciences, VIT University, Vellore – 632 014 (India)
Polycrystalline Ni-Mn-Ga thin films have been deposited on Si (100) substrate with different film thickness. The influence of film thickness on the phase structure and magnetic domain of the films has been examined by scanning electron microscope, atomic force microscopy and magnetic force microscopy. Analysis of structural parameters indicates that the film at lower thickness exhibits the coexistence of both austenite and martensite phase, whereas at higher thickness L1{sub 2} cubic non magnetic phase is noticed. The grains size and the surface roughness increase along with the film thickness and attain the maximum of 45 nm and 34.96 nm, respectively. At lower film thickness, the magnetic stripe domain is found like maze pattern with dark and bright images, while at higher thickness the absence of stripe domains is observed. The magnetic results reveal that the films strongly depend on their phase structure and microstructure which influence by the film thickness.
- OSTI ID:
- 22608711
- Journal Information:
- AIP Conference Proceedings, Vol. 1731, Issue 1; Conference: DAE solid state physics symposium 2015, Uttar Pradesh (India), 21-25 Dec 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Recrystallization and martensitic transformation in nanometric grain size Cu-Al-Ni thin films grown by DC sputtering at room temperature
Preliminary Phase Field Computational Model Development