Magnetic studies of nickel ferrite nanoparticles prepared by sol-gel technique
Ni-ferrite nanoparticles were synthesized by sol–gel technique by varying the solvent concentration. X-ray diffraction studies confirmed the phase purity in the samples. The lattice constant and grain size were found to be in the range of 0.833-0.834 nm and 14-26 nm respectively. There was no systematic variation in magnetization value with the solvent concentration and grain size. The highest magnetization, remanence and coercivity values of 60 emu/g, 12 emu/g and 180 Oe respectively were observed at 300K in the present study for the sample prepared in 75ml of solvent. The observed magnetization value is 20% higher than the bulk value of 50 emu/g. The magnetization, coercivity and remanence values were enhanced at 60K compared to those at 300K. The observed high magnetization value in the nanoparticles can be explained on the basis of modified cation distribution in the lattice sites. The enhanced magnetic properties at 60K may be understood due to the reduced thermal fluctuation and increased anisotropy at low temperature.
- OSTI ID:
- 22606642
- Journal Information:
- AIP Conference Proceedings, Vol. 1728, Issue 1; Conference: ICC 2015: International conference on condensed matter and applied physics, Bikaner (India), 30-31 Oct 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis and Characterization of Nickel-Substituted Cobalt Ferrite Nanoparticles Using Sol–Gel Auto-combustion Method
Magnetic studies of CuFe{sub 2}O{sub 4} nanoparticles prepared by co-precipitation method