Effect of microwave-assisted sintering on dielectric properties of CaCu{sub 3}Ti{sub 4}O{sub 12} ceramic
Journal Article
·
· AIP Conference Proceedings
- Department of Applied Physics, Guru Jambheshwar University of Science & Technology, Hissar 125001, Haryana (India)
- Matu Ram Institute of Engineering and Management, Rohtak (India)
In this present work, CaCu{sub 3}Ti{sub 4}O{sub 12} (CCTO) was synthesized by conventional solid-state reaction technique. The synthesis process was carried out in two phases; by conventional process (calcination and sintering at 1080°C for 10 hours) and phase II involves the micro assisted pre sintering of conventionally calcined CCTO for very short soaking time of 30 min at 1080°C in a microwave furnace followed by sintering at 1080°C for 10 hours in conventional furnace. X-ray diffraction (XRD) patterns confirmed the formation of single phase ceramic. Dielectric properties were studied over the frequency range from 50Hz -5MHz at temperatures (273K-343K). It was observed that pre- microwave sintering enhance the dielectric constant values from 10900 to 11893 and respectively reduces the dielectric loss values from 0.49 to 0.34 at room temperature(1 KHz). CCTO ceramics which are found desirable for many technological applications. The effect is more pronounced at low frequencies of applied electric field.
- OSTI ID:
- 22606258
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1731; ISSN 0094-243X; ISSN APCPCS
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microwave dielectric properties of CaCu{sub 3}Ti{sub 4}O{sub 12}-Al{sub 2}O{sub 3} composite
Development of Dielectric Material with Ceramic Matrix Composite (CMC) Produced from Kaolinite and CaCu{sub 3}Ti{sub 4}O{sub 12} (CCTO)
Intrinsic and extrinsic relaxation of CaCu{sub 3}Ti{sub 4}O{sub 12} ceramics: Effect of sintering
Journal Article
·
Tue Jul 19 00:00:00 EDT 2016
· AIP Conference Proceedings
·
OSTI ID:22608472
Development of Dielectric Material with Ceramic Matrix Composite (CMC) Produced from Kaolinite and CaCu{sub 3}Ti{sub 4}O{sub 12} (CCTO)
Journal Article
·
Tue May 20 00:00:00 EDT 2008
· AIP Conference Proceedings
·
OSTI ID:21143307
Intrinsic and extrinsic relaxation of CaCu{sub 3}Ti{sub 4}O{sub 12} ceramics: Effect of sintering
Journal Article
·
Sun Nov 14 23:00:00 EST 2010
· Journal of Applied Physics
·
OSTI ID:21537940