Use of aluminum oxide as a permeation barrier for producing thin films on aluminum substrates
- Consultant, J. L. Provo Consulting, Trinity, Florida 34655-7179 (United States)
Aluminum has desirable characteristics of good thermal properties, good electrical characteristics, good optical properties, and the characteristic of being nonmagnetic and having a low atomic weight (26.98 g atoms), but because of its low melting point (660 °C) and ability as a reactive metal to alloy with most common metals in use, it has been ignored as a substrate material for use in processing thin films. The author developed a simple solution to this problem, by putting a permeation barrier of alumina (Al{sub 2}O{sub 3}) onto the surface of pure Al substrates by using a standard chemical oxidation process of the surface (i.e., anodization), before additional film deposition of reactive metals at temperatures up to 500 °C for 1-h, without the formation of alloys or intermetallic compounds to affect the good properties of Al substrates. The chromic acid anodization process used (MIL-A-8625) produced a film barrier of ∼(500–1000) nm of alumina. The fact that refractory Al{sub 2}O{sub 3} can inhibit the reaction of metals with Al at temperatures below 500 °C suggests that Al is a satisfactory substrate if properly oxidized prior to film deposition. To prove this concept, thin film samples of Cr, Mo, Er, Sc, Ti, and Zr were prepared on anodized Al substrates and studied by x-ray diffraction, Rutherford ion back scattering, and Auger/argon sputter surface profile analysis to determine any film substrate interactions. In addition, a major purpose of our study was to determine if ErD{sub 2} thin films could be produced on Al substrates with fully hydrided Er films. Thus, a thin film of ErD{sub 2} on an anodized Al substrate was prepared and studied, with and without the alumina permeation barrier. Films for study were prepared on 1.27 cm diameter Al substrates with ∼500 nm of the metals studied after anodization. Substrates were weighed, cleaned, and vacuum fired at 500 °C prior to use. The Al substrates were deposited using standard electron beam cold crucible evaporation techniques, and after deposition the Er film was hydrided with D{sub 2} gas using a standard nonair exposure hydriding technique. All processing was conducted in an all metal ion pumped ultrahigh vacuum system. Results showed that e-beam deposition of films studied onto Al substrates could be successfully performed, if a permeation barrier of Al{sub 2}O{sub 3} from 500 to 1000 nm was made prior to thin film deposition up to temperatures of 500 °C for 1-h. Hydrides also, could be produced with full gas/metal atomic ratios of ∼2.0 as evidenced by the ErD{sub 2} films produced. Thus, the use of a simple permeation barrier of Al{sub 2}O{sub 3} on Al substrates prior to additional metal film deposition was proven to be a successful method of producing both thin metal films and hydride films of various types for many applications.
- OSTI ID:
- 22592870
- Journal Information:
- Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films, Vol. 34, Issue 4; Other Information: (c) 2016 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA); ISSN 0734-2101
- Country of Publication:
- United States
- Language:
- English
Similar Records
Processing effects on microstructure in Er and ErD2 thin-films.
Processing effects on microstructure in Er and ErD2 thin-films